牌号简介 About |
---|
APTIV® 1300薄膜是由Victrex Peek聚合物制成的未填充半晶体薄膜的黑色版本。该薄膜为超高性能应用领域的工程师提供了一种材料解决方案,为APTIV 1000天然产品提供了另一种选择。APTIV® 1300薄膜具有独特的性能组合,提供高温性能、重量轻、机械强度、耐用性、优异的辐射、水解和耐化学性、电绝缘、耐磨损性、优异的高纯度屏障性能、不使用阻燃剂的良好易燃性。燃烧产物的低毒性和薄膜形式的低吸湿性。固有的无卤素和易加工性使APTIV薄膜成为原始设备制造商、我们的客户和最终用户的技术推动者。 APTIV® 1300 film is the black version of unfilled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications offering an alternative option to the APTIV 1000 natural product. APTIV 1300 film has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products and low moisture absorption in a film format. Inherently halogen free and providing ease of processing makes APTIV films a technology enabler for OEMs, our customers and end users. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.30 | g/cm³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
MD:200℃,50.0 µm MD:200℃,50.0 µm |
< 2.0 | % | |
TD:200℃,50.0 µm TD:200℃,50.0 µm |
< 2.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness Film thickness |
50 to 100 µm | ||
拉伸模量 Tensile Modulus Tensile Modulus |
ISO 527-3 | ||
MD,23℃,50 µm MD,23℃,50 µm |
2500 | MPa | ISO 527-3 |
TD,23℃,50 µm TD,23℃,50 µm |
MPa | ISO 527-3 | |
MD,23℃,100 µm MD,23℃,100 µm |
MPa | ISO 527-3 | |
TD,23℃,100 µm TD,23℃,100 µm |
MPa | ISO 527-3 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-3 | ||
MD,断裂 brk,23℃,50 µm MD, fracture BRK, 23 ℃, 50 µ m |
MPa | ISO 527-3 | |
TD,断裂 brk,23℃,50 µm TD, fracture BRK, 23 ℃, 50 µ m |
MPa | ISO 527-3 | |
MD,断裂 brk,23℃,100 µm MD, fracture BRK, 23 ℃, 100 µ m |
MPa | ISO 527-3 | |
TD,断裂 brk,23℃,100 µm TD, fracture BRK, 23 ℃, 100 µ m |
MPa | ISO 527-3 | |
拉伸应变 Tensile Strain Tensile Strain |
ISO 527-3 | ||
MD,断裂 brk,23℃,50 µm MD, fracture BRK, 23 ℃, 50 µ m |
% | ISO 527-3 | |
TD,断裂 brk,23℃,50 µm TD, fracture BRK, 23 ℃, 50 µ m |
% | ISO 527-3 | |
MD,断裂 brk,23℃,100 µm MD, fracture BRK, 23 ℃, 100 µ m |
% | ISO 527-3 | |
TD,断裂 brk,23℃,100 µm TD, fracture BRK, 23 ℃, 100 µ m |
% | ISO 527-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
23 ℃,0.05 mm 23 ℃,0.05 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
23 ℃,0.05 mm 23 ℃,0.05 mm |
kV/mm | ASTM D149 | |
补充信息 Supplementary Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
抗穿刺性 Puncture Resistance Puncture Resistance |
|||
23℃,50.0 µm 23℃,50.0 µm |
kJ/m² | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 TM-VX-84 |
3 100 V |
4 6.25 mm electrode |
【新闻资讯】查看全部
LG化学开发阻止电池热失控的先进塑料材料
2022-05-12 近日,LG化学宣布,凭借其专有技术和制造工艺,成功开发出一种防止热变形的阻燃工程塑料材料,目前是世界最长延迟电动汽车电池热失控时间的电池组塑料材料,拓展产品市场。 据 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |