牌号简介 About |
---|
Polytrope Str 1032eu树脂是一种经济高效、高熔融强度的热塑性TPO材料,其抗冲击性和刚度与ABS相似,但具有尺寸稳定性、耐化学性和耐候性等优点。它可以在光滑或纹理表面挤压,或与增强聚烯烃帽树脂共同挤压,以进一步定制其耐用性,外观,或内部和外部应用的感觉。Polytrope Str 1032eu在挤压和热成型过程中提供非常光滑的表面的能力使其非常适合用装饰膜层压工艺。它也很容易上色,可通过标准TPO油漆系统进行喷漆。 POLYTROPE STR 1032EU resin is a cost efficient, high melt strength thermoformable TPO material that provides an economical balance of impact resistance and stiffness similiar to ABS, but provides the benefits of dimensional stability, chemical and weathering resistance characteristic of TPO materials. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1032EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.13 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.70 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
23℃,3.2 mm,24 hrs 23℃,3.2 mm,24 hrs |
0.80 to 1.2 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,23℃ Yield, 23 ℃ 3 |
23.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain 3 |
|||
断裂,233℃ Fracture, 233 ℃ 3 |
430 | % | ISO 527-2 |
弯曲模量 Bending modulus 4 |
|||
弦,23℃ String, 23 ℃ 4 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
流量,-30℃,3.2mm,注塑成型 Flow rate, -30 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
流量,23℃,3.2mm,注塑成型 Flow rate, 23 ℃, 3.2mm, injection molding |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
0℃,Total Energy,Ductile Failure 0℃,Total Energy,Ductile Failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ASTM E831 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,3180 µm,热塑,光滑 60 °, 3180 µ m, thermoplastic, smooth |
ISO 2813 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(8 inch span,two point support,149℃,3.20 mm) Heat Sag(8 inch span,two point support,149℃,3.20 mm) |
mm | ASTM D3769 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 A |
3 类型 1, 2.0 in/min |
4 类型1A, 0.079 in/min |
【新闻资讯】查看全部
匹克发布国际首款3d打印聚氨酯鞋
2017-05-15 近日,匹克体育在北京发布了旗下首款3D打印跑鞋,这款创新跑鞋,也成为中国首款市售的3D打印跑鞋,让消费者看到了3D打印科技即将改变的未来。据介绍,此次匹克发布的3D打印跑鞋,以旗下最为畅销的缓震跑鞋“悦跑五代”为原型,辅以3D打印技术实现科技创新。在继承悦跑五代透气、舒适穿着体验的同时,3D打印技术制成的3D材料中底,通过SLS激光烧结技术以及更为弹性轻质的TPU粉末成型的3D打印跑鞋,既能保证跑步时中底所需的强度,同时由于材质的轻质又能提供出色的柔软度及缓冲回弹性能。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |