牌号简介 About |
---|
EBA Alcudia PA-1715是一种适用于一般挤出和注塑应用的共聚物,在这些应用中需要良好的加工性、柔韧性和良好的机械性能。丙烯酸丁酯含量为17%。它含有抗氧化添加剂。典型应用挤出(型材、片材)注射成型微孔泡沫推荐熔融温度180°C。PA-1715的加工特性与低密度聚乙烯相似,推荐使用传统的聚乙烯挤出机。各生产线的加工条件应得到优化。 EBA ALCUDIA® PA-1715 is a copolymer suitable for general extrusion and injection moulding applications where good processability, flexibility and very good mechanical properties are required. The butyl acrylate content is 17%. It contains antioxidant additives. TYPICAL APPLICATIONS Extrusion (profiles, sheets) Injection moulding Microcellular foams Recommended melt temperature 180°C. Processing characteristics of PA-1715 are similar to LDPE and conventional polyethylene extruders are recommended. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ISO 1133 |
丁酯丙烯酸成分 Butyl acrylate composition |
17.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
68.0 | ℃ | ISO 306/A |
熔融温度 Melting temperature |
95.0 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
日上集团:取得阿曼LIWA塑料工业综合体推销订单
2016-09-29 公司控股子公司收到CB IKoreaYuhanhoesaLimited关于阿曼LIWA塑料工业综合体(LPIC EPC1SCU工程)的《采购订单》,订单总金额2436万美金,占公司2015年度营业收入的12.64%,订单主要交货时间在2017年度。项目的中标是公司设备钢结构业务在设计体系、项目执行管理、品质控制、欧美标准等全方位综合实力被国际市场认可的进一步体现。公司前期创出新高后逐步回落,成交量已回到低位水平,关注能否企稳。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |