Semitron ESD 500HR采用专有合成云母增强,具有低摩擦性能、良好的尺寸稳定性和静电耗散特性。每当原始聚四氟乙烯引起放电问题时,Semitron ESD 500HR将提供受控的静电荷排出,同时保持典型的聚四氟乙烯特性,如宽耐化学性和低摩擦系数表面电阻率:1010-1012 ohms/sq热性能至500°F(260°C),热绝缘性极低。摩擦系数宽耐化学性 Reinforced with a proprietary synthetic mica, Semitron ESd 500HR offers an excellent combination of low frictional properties, good dimensional stability and electrostatic dissipation. Whenever virgin PTFE causes electrical discharge problems, Semitron ESd 500HR will provide a controlled bleed-off of static charges while maintaining typical PTFE-properties such as broad chemical resistance and low coefficient of friction Surface resistivity: 1010 - 1012 ohms/sq Thermal performance to 500°F (260°C) Thermally insulative Very low coefficient of friction Broad chemical resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.30 | g/cm³ | ISO 1183 |
吸水率 Water absorption rate |
|||
饱和 saturated |
1.0 到 2.0 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
< 0.10 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
7.5 | kJ/m² | ISO 179-1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
30 | kJ/m² | ISO 179/1eU |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~100℃ MD:23~100℃ |
1/℃ | ||
最高使用温度 Maximum operating temperature |
|||
Air,Continuous Air,Continuous |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲强度 bending strength |
MPa | ||
压缩强度 compressive strength |
|||
1% 应变 1% strain |
MPa | ||
2% 应变 2% strain |
MPa | ||
5% 应变 5% strain |
MPa |
备注 |
---|
2、10°C/min |
【新闻资讯】查看全部
工程塑料市场增长惊人
2018-06-13 市场研究公司Markets and Markets的最新研究报告显示,2016年到2026年期间,全球工程塑料市场将会以年均7.4%的速度快速增长,到2026年全球工程塑料市场将达到近1090亿美元,而相关的专业人士表示,工程塑料市场将拥有如此大的市场,这完全在情理之中。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |