牌号简介 About |
---|
BPD2167是一种不稳定的低密度热塑性聚乙烯。它设计用于“C_ble de fa_ade”应用和一步硅烷交联绝缘。需要在BPD2167中添加一个精心挑选的炭黑和添加剂主批次,以达到最终的“电缆表面”配方。然而,全配方黑色化合物BPD8167在均匀性、老化和锚固试验方面获得最佳性能,只需向其中添加硅烷混合物。 BPD2167 is an unstabilised low density thermoplastic polyethylene. It is designed for use in "Câble de façade" application and one step silane crosslinking insulation. A carefully selected carbon black and additives master batch needs to be added to BPD2167 to reach the final "Cable de Façade" formulation. The best performance in terms of homogeneity, aging and anchorage tests is however obtained with the fully formulated black compound BPD8167, to which only the Silane mixture needs to be added. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.20 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
18.0 | MPa | IEC 60811-1-1 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 500 | % | IEC 60811-1-1 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
1.0E+16 | ohms·cm | ASTM D257 |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
50 Hz 50 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
ASTM D150 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
一种合适在尼龙、树脂、塑料行业尾气处置的RTO技术
2017-07-20 全球著名的尼龙、ABS材料、PBT树脂企业日本某株式会社,采用了上海安居乐环保科技股份有限公司研发的GRTO蓄热式热力氧化处理VOCs。这是继全球著名的复合树脂生产企业美国艾蒂后又一跨国公司采用GRTO技术。标志着GRTO技术在尼龙、树脂、聚酯纤维等高分子化学行业VOCs治理领域取得重大突破! 尼龙、树脂、塑料行业生产中产生的废气主要成分有:苯酚、环己烷、丙烯腈、丁二烯、苯乙烯等,其排放特点为:废气浓度变化较大,波动频繁。在环保法规日益严苛的氛围下,采用蓄热焚烧(RTO)技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |