牌号简介 About |
---|
35%玻璃纤维增强Vectra级,具有非常低的排气量、非常高的热变形温度(335°C)和刚度。典型的应用包括灯具插座、光束器用透镜、连接器、继电器、开关、线圈绕线管等电气和电子部件以及发动机罩下的应用。化学缩写符合ISO 1043-1:LCP固有阻燃性UL列表V-0,根据UL 94火焰试验,0.28mm厚天然阻燃。根据UL 746B的相对温度指数(RTI):电气130°C,机械130°C。UL=保险商实验室(美国) 35% glass reinforced Vectra grade with very low outgassing, very high heat deflection temperature (335°C) and stiffness. Typical applications are lamp sockets, lens holders for beamers, electrical and electronic parts like connectors, relays, switches, coil bobbins and also under the hood applications. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural at 0.28mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.67 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.40 | % | ISO 294-4 |
MD MD |
0.10 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
4.0E-3 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
7.0E-3 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
|||
1% 应变 1% strain |
MPa | ISO 604 | |
断裂弯曲应变 Fracture bending strain |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
路博润德克萨斯州聚异丁烯项目破土开工
2017-04-05 3月22日,路博润在美国德克萨斯州鹿园新建的聚异丁烯(PIB)厂区破土动工。 根据路博润之前公布的10年分阶段投资计划,将持续改造其添加剂基础设施,而此厂区的建设正是其中一项举措。 新厂区预计在2019年上半年全面投入使用。 它将为路博润提供高反应性聚异丁烯(HR PIB)生产能力,这种聚异丁烯是下一代分散剂和润滑剂的关键原料。 来源 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |