牌号简介 About |
---|
Adsyl 5 C 33 F是一种高级聚烯烃,专门设计用于共挤薄膜应用中的密封或金属化层。该等级具有极低的密封启动温度和良好的光学性能。不含滑脱或抗阻塞添加剂,不含硬脂酸钙。有关监管信息,请参阅Adsyl 5 C 33 F产品管理公告(PSB)。 Adsyl 5 C 33 F is an advanced polyolefin, specially designed for use as a sealing or metallized layer in co-extruded film applications. This grade features a very low seal initiation temperature and good optics. It does not contain slip or anti-block additives and it is Calcium Stearate free. For regulatory information please refer to Adsyl 5 C 33 F Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 |
密度 Density |
0.900 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.5 | g/10min | ASTM D1238 |
230℃,2.16kg 230℃,2.16kg |
5.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus 2 |
|||
1% 正割 1% secant 2 |
648 | MPa | ASTM D790-A |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-3/25 | ||
MD,50 µm,铸造薄膜 MD, 50 µ m, cast thin film |
MPa | ISO 527-3/25 | |
TD,50 µm,铸造薄膜 TD, 50 µ m, cast thin film |
MPa | ISO 527-3/25 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
屈服 yield |
MPa | ASTM D638 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
屈服 yield |
% | ASTM D638 | |
MD,断裂,50 µm,铸造薄膜 MD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,铸造薄膜 TD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
MD,屈服,50 µm,铸造薄膜 MD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,屈服,50 µm,铸造薄膜 TD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
始封温度 Initial sealing temperature |
℃ | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
【新闻资讯】查看全部
中美贸易战或影响聚碳酸酯(PC)价钱
2018-04-13 近期聚碳酸酯(PC)的市场价格始终保持在高位态势。目前在亚洲市场,每吨聚碳酸酯价格已经达到了3800到3900美元之间。较二月价格上涨5%左右。由于北美地区生产设备的故障以及中国地区新项目的延期,使得PC库存短缺的状况或将持续。因而价格有可能出现进一步上涨。 由于其原料双酚A的需求预计不会出现较大变化,因而双酚A价格预计未来不会出现上扬。由于中美贸易战持续升温,中国对美国的化工品实施报复性关税。这使得美国的PC材料也在美国关税补偿范围之内。加之新材料的出现,短期内PC需求量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |