牌号简介 About |
---|
3M Dyneon PFA 6502TAZ是一种用于压缩成型的氟热塑性树脂。当需要更长的停留时间或更高的温度时,PFA 6502TAZ具有宽的处理窗口和极好的颜色稳定性。这种团聚形式也可用于配制。特点和优点卓越的热稳定性宽加工窗口改进的模具释放良好的应力抗裂光滑表面良好的透明度工艺目标:压缩成型和混合 3M™ Dyneon™ PFA 6502TAZ is a fluorothermoplastic resin for compression molding applications. PFA 6502TAZ has a wide processing window with excellent color stability when longer residence times or higher temperatures are required. This agglomerate form can also be used for compounding. Features and Benefits Excellent thermal stability Broad processing window Improved mold release Good stress crack resistance Smooth surfaces Good transparency Process targets: compression molding and blending |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.15 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
0.85 | g/cm³ | DIN 53466 |
熔体质量流动速率 Melt Flow Rate |
|||
372℃,5.0kg 372℃,5.0kg |
2.0 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
308 | ℃ | ASTM D4591 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
> 95 | % | ASTM D2863 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
金发科技新增4000吨高温尼龙材料及800吨PPSU材料产能!
2021-07-28 搜料网资讯: 从近几年国内改性塑料以及树脂厂商的布局来看,做树脂的逐渐向改性塑料延伸,改性塑料逐渐向树脂合成发展。比如金发科技有LCP、高温尼龙、PP等的合成,普利特有L |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-3M™ Dyneon™ Fluoroplastic PFA 6502TAZ证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)