牌号简介 About |
---|
聚偏氟乙烯(PVDF)是一种理想的跨行业的多种应用。广泛应用于化工、电线电缆、半导体、石油和天然气等行业。聚偏氟乙烯在汽车、建筑、电子、食品加工、制药和电池等领域也得到了广泛的认可。聚偏氟乙烯60080001具有天然的纯度和抗各种腐蚀性液体和溶剂的化学性能。其特点是对各种腐蚀性液体和溶剂具有优异的耐化学性,表面光滑,防污,抗渗透性好,注射成型等级优良,强度和尺寸稳定性好,颜色稳定性好。 Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, pharmaceutical and batteries. 3M™ Dyneon™ PVDF 6008/0001 is easily processed under a variety of conventional thermoplastic conversion techniques, being particularly suitable for extrusion. PVDF 6008/0001 is inherently pure and chemically resistant against a variety of aggressive fluids and solvents. PVDF 6008/0001 exhibits excellent dimensional stability, abrasion resistance and high strength, and maintains its mechanical properties at elevated temperature. Features and Benefits Excellent chemical resistance to a variety of aggressive fluids and solvents Smooth, anti-fouling surfaces Good permeation resistance Injection molding grade Excellent strength and dimensional stability Good color stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.78 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ASTM D1238 |
230℃,5.0kg 230℃,5.0kg |
24 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
3.0 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.040 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D3418 | ||
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ASTM D3418 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D3418 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
|||
3.0 mm 3.0 mm |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.079 in/min |
【新闻资讯】查看全部
科思创CMF美学色板荣获德国设计奖
2021-11-22 搜料网资讯: ● 旨在通过聚碳酸酯美观性与功能性,激发设计师灵感 德国设计委员会日前宣布,科思创CMF美学色板荣获其2022德国设计奖卓越产品设计-材料与表面处理奖项。科思创期望 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-3M™ Dyneon™ Fluoroplastic PVDF 60080001证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)