牌号简介 About |
---|
CONATHANE® EN-2550是一种由两部分组成的填充聚氨酯树脂系统,用于铸造高压变压器和封装或封装电子设备。该系统具有良好的室温处理性能、良好的工作寿命和最小的加工危害。CONATHANE® EN-2550可以在室温或高温下固化,而不会形成空隙。所述固化物具有优异的耐水性和抗热震性。该系统的其他有益特性包括:低温、固化过程中的低应力、低收缩和非常好的电性能。 CONATHANE EN-2550 is a two-part, filled polyurethane resin system formulated for casting high-voltage transformers and potting or encapsulating electronic devices. The system features good handling properties at room temperature, good working life, and minimum processing hazards. CONATHANE EN-2550 can be cured at room or elevated temperatures without the formation of voids. The cured compound has excellent water resistance, and is resistant to thermal shock. Other beneficial characteristics of this system include low exotherm, low stresses during cure, low shrinkage, and very good electrical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 3 |
1.23 | g/cm³ | |
-- -- 4 |
1.52 | g/cm³ | |
吸水率 Water absorption rate |
|||
25℃,24hr ,水中 25 ℃, 24 hours, in water |
0.075 | % | |
7days 7days |
0.19 | % | |
25℃,7days,水中 25 ℃, 7 days, in water |
1.5 | % | |
固体含量 Solid content |
|||
-- -- 3 |
% | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
kN/m | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
|||
-- -- 5 |
ohms | ||
-- -- 6 |
ohms | ||
-- -- 7 |
ohms | ||
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
60 ℃ 60 ℃ |
ohms·cm | ||
120 ℃ 120 ℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
0.406 mm 0.406 mm |
kV/mm | ||
0.813 mm 0.813 mm |
kV/mm | ||
1.57 mm 1.57 mm |
kV/mm | ||
介电常数 Dielectric constant |
|||
25 ℃,100 Hz 25 ℃,100 Hz |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,1 MHz 25 ℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
25℃,100 Hz 25℃,100 Hz |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,1 MHz 25℃,1 MHz |
|||
耐电弧性 Arc resistance |
sec | ||
绝缘电阻 insulation resistance |
|||
25℃ 25℃ |
ohms | ||
60℃ 60℃ |
ohms | ||
120℃ 120℃ |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ 3 |
cP | ||
25℃ 25℃ 4 |
cP | ||
25℃ 25℃ 8 |
cP | ||
40℃ 40℃ 8 |
cP | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
冷热冲击测试 Test - 10 cycles,-65℃ to 130℃ Cold and hot shock test -10 cycles, -65 ℃ to 130 ℃ |
|||
工作期限 Working period |
|||
234 gm mass to 100000 cps,25℃ 234 gm mass to 100000 cps,25℃ |
min | ||
抗真菌性 Antifungal activity |
|||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Linear Shrinkage Linear Shrinkage |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Resin |
3 Hardener |
4 90°C |
5 60°C |
6 25°C |
7 Mixed |
【新闻资讯】查看全部
国家统计局:1-2月份全国规模以上工业企业利润增长5.0%
2022-03-28 国家统计局网站3月27日消息,1-2月份,全国规模以上工业企业实现利润总额11575.6亿元,同比增长5.0%。 1-2月份,规模以上工业企业中,国有控股企业实现利润总额4157.8亿元,同比增长 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |