牌号简介 About |
---|
这种茂金属线性低密度聚乙烯是一种乙烯-己烯共聚物,为吹塑薄膜应用量身定制,要求:良好的拉伸性能、优异的韧性、表面印刷硬度、典型的吹塑薄膜应用包括:重型包装工业包装机构包装 This metallocene linear low density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require: Good tensile properties Exceptional toughness Surface printing Stiffness Typical blown film applications include: Heavy duty packaging Industrial packaging Institutional packaging |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.95 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.80 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
221 | MPa | ASTM D882 |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 2 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
℃ | ASTM F88 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,25.4 µm,吹塑薄膜 60 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
2 Temperature at which 0.3 lb/in heat seal strength is achieved. 0.5 s dwell, 30 psi pressure, 11.8 in/min separation rate. |
【新闻资讯】查看全部
伟星新材:净利润创新高 劲增38.5%
2017-02-21 据浙江伟星新型建材股份有限公司(简称“伟星新材”)最新发布的2016年业绩快报显示,2016年1-12月伟星新材营业收入达33.2亿元,同比增长20.9%,归属上市公司股东净利润6.7亿元,同比增长38.5%。 其中第四季度实现营业收入11.8亿元,同比增长28.4%,环比增长43.1%,归属上市公司股东净利润2.3亿元,同比增长46.4%,增长14.8%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |