技术参数 Technical Data | |||
---|---|---|---|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电正切 Dielectric tangent |
|||
106Hz 106Hz |
0.009 | ASTM D-150 | |
60Hz 60Hz |
0.0004 | ASTM D-150 | |
介电率 Dielectric constant |
|||
60Hz 60Hz |
2.95 | ASTM D-150 | |
106Hz 106Hz |
2.9 | ASTM D-150 | |
绝缘破坏强度 Insulation failure strength |
|||
快速加压值厚度1.6mm Quick pressurization value thickness 1.6mm |
30 | KV/mm | ASTM D-149 |
体积电阻率 Volume resistivity |
1016Ω.cm | ASTM D-257 | |
耐导电径迹性(CTI) Conductive Track Resistance (CTI) |
V | IEC 112 | |
耐电弧性 Arc resistance |
sec | ASTM D-495 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
Mpa(kgf/cm²) | ASTM D-790 | |
拉伸强度 tensile strength |
Mpa(kgf/cm²) | ASTM D-638 | |
耐冲击强度值 Impact strength value |
|||
艾氏、带缺口厚度3.2mm Aishi, with a notch thickness of 3.2mm |
j/m(kgf·cm/cm) | ASTM D-256c | |
艾氏、带缺口厚度6.4mm AISI, with a notch thickness of 6.4mm |
j/m(kgf·cm/cm) | ASTM D-256 | |
洛氏硬度 Rockwell hardness |
M标度 | ASTM D-785 | |
拉伸率 Stretching rate |
ASTM D-638 | ||
压缩强度 compressive strength |
Mpa(kgf/cm²) | ASTM D-695 | |
弯曲强度 bending strength |
Mpa(kgf/cm²) | ASTM D-790 | |
拉伸模量 Tensile modulus |
Mpa(kgf/cm²) | ASTM D-638 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 proportion |
ASTM D-792 | ||
透光率 Transmittance |
|||
厚度3mm Thickness 3mm |
% | ASTM D-1003 | |
阻燃性 Flame retardancy |
|||
厚度1.47mm Thickness 1.47mm |
UL 94 | ||
厚度3.05mm Thickness 3.05mm |
UL 94 | ||
折射率 Refractive index |
ASTM D-542 | ||
加工性能 Processing performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
成型收缩率 Forming shrinkage rate |
% | ASTM D-955 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
负荷挠曲温度 Load deflection temperature |
|||
负荷1.813MPa(18.6kgf/cm) Load 1.813MPa (18.6kgf/cm) |
°C | ASTM D-648 | |
负荷0.451MPa(4.6kgf/cm) Load 0.451MPa (4.6kgf/cm) |
°C | ASTM D-648 | |
温度指数 Temperature index |
|||
厚度1.47mm Thickness 1.47mm |
°C | UL 746B | |
厚度1.47mm Thickness 1.47mm |
°C | UL 746B | |
线膨胀系数 Linear expansion coefficient |
10-5cm/cm/℃ | ASTM D-696 | |
基本性能 Basic performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water absorption rate |
|||
24hr,in 23℃ 24hr,in 23℃ |
% | ASTM D-570 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
再使用PET领域异军突起的竟然再生涤纶短纤维(RPSF)
2017-07-12 塑料的回收利用是指将已废弃塑料转化成可再利用形式的过程。废弃的塑料可以是像瓶子或者容器一样的刚性材质;也可以是像薄膜或者包装纸一样的非刚性材质。塑料回收市场可以细分为树脂类,比如PET。聚对苯二甲酸乙二醇酯缩写为PET,是聚酯系列中最常见的热塑性聚合物树脂,用于制造服装纤维、乘放液体和食物的容器,多采用热压成型方法制造。 根据透明度市场研究的报告,再生PET主要用于制造聚酯纤维、捆绑包装带和非食品容器。大多数热塑性塑料可以循环使用;因为大量的碳酸饮料瓶和饮用水瓶以PET为原 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |