牌号简介 About |
---|
本产品为30%玻纤增强及15%聚四氟乙烯PTFE增强的改性聚邻苯二甲酰胺材料,具有优异的热稳定性、自润滑性和耐磨性,同时兼顾良好的强度。可以广泛应用在精密电子件结构件等塑胶件产品上。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.58 | g/cm³ | ASTM D792 |
密度 Density Density |
1.57 | g/cm³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
TD:24 hrs TD:24 hrs |
0.80 to 1.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.20 to 0.40 | % | ASTM D955 |
吸水率 Water Absorption Water Absorption |
|||
平衡 ,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.25 | % | ISO 62 |
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
ASTM D638 | ||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ASTM D638 | |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk Broken BRK |
MPa | ISO 527-2/5 | |
断裂 brk Broken BRK |
MPa | ASTM D638 | |
屈服 yld Yield yld |
MPa | ISO 527-2/5 | |
屈服 yld Yield yld |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ISO 527-2/5 | |
断裂 brk Broken BRK |
% | ASTM D638 | |
屈服 yld Yield yld |
% | ISO 527-2/5 | |
屈服 yld Yield yld |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
断裂 brk,50 mm跨度 Broken BRK, 50 mm span |
MPa | ASTM D790 | |
屈服 yld,50 mm跨度 Yield yld, 50 mm span |
MPa | ASTM D790 | |
摩擦系数 Frictional coefficient Frictional coefficient |
ASTM D3702 Modified | ||
动态 dynamic |
ASTM D3702 Modified | ||
静态 static state |
ASTM D3702 Modified | ||
磨损因数 Wear factor Wear factor |
ASTM D3702 Modified | ||
Ring Ring |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
Washer Washer |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Falling dart impact with measuring instruments Falling dart impact with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multiaxial Impact Multiaxial Impact |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
宁夏中卫工业园区:一张图“链”出一个绿色园区
2021-08-10 搜料网资讯: 图为调研座谈会现场 将产业关联度作为硬指标,这在石油和化工园区可持续发展中国行调研组走访过的中西部园区里并不多见,很多园区是以同类或几类主导产品为主的集 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |