牌号简介 About |
---|
Radel® R-5800是Radel聚苯砜(PPSU)的高熔体流动级。它特别适用于需要长流动长度和薄壁的零件。Radel树脂具有优异的水解稳定性和韧性,优于其他商用高温工程树脂。它们还提供高偏转温度和优异的抗环境应力开裂性能。Radel聚合物具有固有的阻燃性,具有优异的热稳定性和良好的电气性能。附加的Radel等级包括透明注射成型等级(R-5000)、不透明通用注射成型等级(R-5100)和透明挤出等级(R-5500)。自然色/透明色:Radel® R-5800 NT额外定制颜色 Radel® R-5800 is a high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptional hydrolytic stability and toughness superior to other commercially-available, high-temperature engineering resins. They also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Additonal Radel® grades include a transparent injection molding grade (R-5000), an opaque, general purpose, injection molding grade (R-5100) and a transparent, extrusion grade (R-5500). Natural/Transparent: Radel® R-5800 NT Additional Made-to-Order Colors Available |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
365℃,5.0kg 365℃,5.0kg |
20 to 28 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡 balance |
1.1 | % | ASTM D570 |
24hr 24hr |
0.37 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
屈服,3.18 mm Yield, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
5% 应变,3.18 mm 5% strain, 3.18 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
拉伸冲击强度 Tensile impact strength |
|||
3.18 mm 3.18 mm |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature 2 |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
3.18 mm 3.18 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
0.0254 mm 0.0254 mm |
kV/mm | ASTM D149 | |
3.18 mm 3.18 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
3.18 mm,60 Hz 3.18 mm,60 Hz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.76 mm 0.76 mm 3 |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Steam Sterilization(w/ Morpholine) Steam Sterilization(w/ Morpholine) 4 |
Cycles |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 升温速率36 °F(20 °C)时/分钟 |
3 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
4 周期完成,无开裂、裂纹或破裂。 蒸气消毒条件: - 温度:270 °F(132 °C) - 时间: 30分钟/周期 - 蒸汽压力: 27 PSIG (0.19兆帕) -应力水平:弯曲1000 psi (7.0兆帕) - 添加剂:50 ppm吗啉 |
【新闻资讯】查看全部
兰州石化橡胶厂一季度苯乙烯产销两旺
2018-04-17 从兰州石化橡胶厂获悉,一季度完成苯乙烯产量16100吨,销售9019吨,分别完成计划的105.92%和109.99%,双双创造历史同期最好水平,为创效增益和有序完成全年生产任务起好步、开好头。 苯乙烯是兰州石化橡胶厂合成橡胶和合成树脂生产的主要单体原料,其产量的多少与质量的好坏直接左右着下游生产和市场商品供给。过去由于自身需求量大,投入市场的占比较小。从2014年开始,合成橡胶和合成树脂市场一度疲软,价格持续下滑,严重制约了装置有序生产和创效能力。为此,这个厂本着保增长,保 |
兰州石化橡胶厂一季度苯乙烯产销两旺 从兰州石化橡塑厂获知,一季度进行苯乙烯生产量16100吨,市场销售9019吨,各自进行方案的105.92%和109.99%,同时征服世界当期最好是水准,为创效增益值和井然有序进行全年度生产每日任务起好步、开开好局。 苯乙烯是兰州石化橡塑厂丁苯橡胶和树脂材料生产的关键单个原料,其生产量的是多少与品质的优劣立即上下着中下游生产和销售市场产品提供。以往因为本身需要量大,投放市场的占较为小。从二零一四年刚开始,丁苯橡胶和树脂材料销售市场一度皮软,价钱不断下降,比较严重牵制了装置井然有序生产和创效能力。因此,这一厂秉着稳增长,保经济效益的发展战略高宽比,宏观经济政策产供销构造,精确把握市场走势,全方位加强生产全过程监管幅度,在确保本身单个原料要求的前提条件下,全力扩展产品营销渠道,为装置超负荷平稳生产出示了前提条件,从而做到苯乙烯产品和本身原料占有率颠倒,使近些年产品占有率均贴近60%,大大的提高了苯乙烯装置的创效能力。 2018至今,兰州石化橡塑厂持续保持上本年度苯乙烯产供销双“更新”的优良趋势,厂部各部门相互配合生产生产车间处理具体难题,监管贯彻落实好各类管理制度,激励生产企业自主创新方式方法,加强流程管理,积极开展劳动竞赛,使装置安全性生产持续保持在可控情况。 在工艺管理上不断进行加工工艺提升和短板科技攻关主题活动,胆大选用新改性剂,全方位提升加工工艺全过程,合理降低高能耗全过程阶段,进一步为商品合格和装置创效出示确保。此外,每星期坚持不懈做好经济活动分析会,对存在的不足制订相对的解决方法和整顿措施,并以企业、厂岗位责任制度大查验为服务平台,催促生产车间、团小组和职位,不断进行装置安全隐患排查和“低老坏”治理不释放压力,依据具体要求制订装置与大发电机组维修保养管理条例,产生以维达、电仪、化工厂、管理方法“四位一体”的监管方式,从而做到非方案泊车频次为零,漏率≤0.25‰下列。一系列管控措施的实行,促使装置加工工艺稳定率持续保持在100%,商品优等品品率100%,职位安全巡检及格率100%,加工工艺中控台达标率均值在99.6%之上,为一季度获得优异的成绩奠定了扎扎实实基本。 来源于:中国新闻网甘肃省 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 印刷电路板维护涂层
- 2019-03-19 78
- Radel® R-5800是Radel聚苯砜(PPSU)的高熔体流动级,材料有良好的水解稳定性
- 阅读全文
印刷电路板维护涂层
2-Radel树脂具有优异的水解稳定性和韧性,优于其他商用高温工程树脂
4-树脂具有高变形温度,与其他无定形材料相比显示出突出的耐环境应力开裂特点
抱歉!暂无数据。