牌号简介 About |
---|
Viton® Extreme™ ETP-600S是Viton ETP-900的改进处理版本,其设计在流体阻力方面尽可能与ETP-900匹配。ETP-600S的单体组成与ETP-900基本相同,但由于优化了聚合物结构,基于Viton® Extreme™ ETP-600S的化合物表现出以下特征:更快的固化速度提高了高剪切速率下的流动性,稍高的拉伸强度提高了对压缩变形等效流体的抵抗力,以及基于在ETP-600S上,可以以用于混合、预成型和成型传统氟弹性体的相同方式容易加工。加工者将注意到,基于ETP-600S的化合物通常混合得稍快,挤出得稍平稳,与基于ETP-900的相同化合物相比,模具粘着力较小。 Viton® Extreme™ ETP-600S is an improved processing version of Viton® ETP-900, designed to match ETP-900 as closely as possible in terms of fluid resistance. The monomer composition of ETP-600S is virtually identical to ETP-900, but due to an optimized polymer architecture, compounds based on Viton® Extreme™ ETP-600S exhibit the following: Faster cure rates Improved flow at high shear rates Slightly higher tensile strength Improved resistance to compression set Equivalent fluid and chemical resistance Compounds based on ETP-600S can be readily processed in the same manner used for mixing, preforming, and molding conventional fluoroelastomers. Processors will note that compounds based on ETP-600S will typically mix slightly faster, extrude somewhat more smoothly, and exhibit less mold sticking than the same compound based on ETP-900. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.82 | g/cm³ | ASTM D792 |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
60 | MU | ASTM D1646 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 2 |
60 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 3 |
75 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 4 |
76 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 6 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
50% 应变,23℃ 50% strain, 23 ℃ 7 , 8 |
MPa | ASTM D412 | |
50% 应变,23℃ 50% strain, 23 ℃ 7 , 9 |
MPa | ASTM D412 | |
50% 应变,23℃ 50% strain, 23 ℃ 7 , 10 |
MPa | ASTM D412 | |
50% 应变,23℃ 50% strain, 23 ℃ 7 , 11 |
MPa | ASTM D412 | |
50% 应变,23℃ 50% strain, 23 ℃ 7 , 12 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 13 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 14 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 15 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 16 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 17 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服,23℃ Yield, 23 ℃ 13 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 14 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 15 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 16 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 17 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 13 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 14 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 15 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 16 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 17 |
% | ASTM D412 | |
压缩形变 Compression deformation |
ASTM D395B | ||
150℃,70 hr 150℃,70 hr |
% | ASTM D395B | |
150℃,336 hr 150℃,336 hr |
% | ASTM D395B | |
200℃,70 hr 200℃,70 hr |
% | ASTM D395B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min |
3 Aged 168 hr at 100°C in 30% potassium hydroxide in water |
4 Aged 168 hr at 150°C in Axle Lubricant with 6% high pH additive |
5 Aged 168 hr at 23°C in MEK |
6 Aged 16 hr at 200°C |
7 Aged 168 hr at 250°C |
8 20 in/min, 老化 MEK 168 hr 在 73°F |
9 20 in/min, 老化 Potassium Hydroxide 30% 168 hr 在 212°F |
10 20 in/min, 老化 Axle Lubricant with 6% High pH Additive 168 hr 在 302°F |
11 20 in/min, 老化 16 hr 在 392°F |
12 20 in/min, 老化 168 hr 在 482°F |
13 老化 MEK 168 hr 在 73°F |
14 老化 Potassium Hydroxide 30% 168 hr 在 212°F |
15 老化 Axle Lubricant with 6% High pH Additive 168 hr 在 302°F |
16 老化 16 hr 在 392°F |
17 老化 168 hr 在 482°F |
【新闻资讯】查看全部
“禁塑令”来了 可降解塑料行业迎风口
2020-09-05 搜料网资讯:明年(2021年)1月1日起,部分城市将率先禁止使用不可 降解塑料 购物袋。受限塑令升级影响,多家上市公司布局可降解塑料相关领域,业内人士认为,该领域具有较大市 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |