牌号简介 About |
---|
PC alloy grade |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.19 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
280℃,5 kg 280℃,5 kg |
21.0 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
Internal Method | ||
TD:4.0 mm TD:4.0 mm |
0.50 to 0.70 | % | 内部方法 |
MD:4.0 mm MD:4.0 mm |
0.50 to 0.70 | % | 内部方法 |
吸水率 Water Absorption Water Absorption |
|||
23℃,24hr 23℃,24hr |
0.22 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk Broken BRK |
MPa | ISO 527-2/50 | |
屈服 yld Yield yld |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ISO 527-2/50 | |
屈服 yld Yield yld |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
ISO 179 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | IEC 60093 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
0.45 mm 0.45 mm |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) Glow Wire Ignitability Temperature (GWIT) |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
沙特基础延续第三年荣膺博鳌亚洲论坛战略合作同伴
2016-01-07 沙特基础工业公司(SABIC)宣布连续第三年成为博鳌亚洲论坛战略合作伙伴并连续第八年参会,以践行对论坛的长期承诺。今天,在博鳌亚洲论坛秘书长周文重主持的新闻发布会上,SABIC副总裁兼北亚区总裁李雷宣布了这一消息。 “SABIC很荣幸在2016年能够再度成为博鳌亚洲论坛年会的战略合作伙伴,协助塑造、推动及支持亚洲的未来发展计划。通过博鳌亚洲论坛的战略对话,我们带着共同的愿景致力于促进亚太区经济体的融合,推动包容和可持续增长,并创生新的可能。在SABIC看来,未来的诸多挑战同 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |