牌号简介 About |
---|
低压建筑电线绝缘用低密度湿固化聚乙烯化合物(CSA RW-90、RWU-90、AC-90、TECK-90)。Pexidan® R/T是一种低密度交联聚乙烯系统,可通过水分固化,由硅烷预接枝的碱化合物A-3001和催化剂母料CAT-009(Sioplas方法)组成。按适当比例(95/5)混合后,两种成分在挤压后形成一种材料,该材料可在70-90°C或甚至环境湿度下暴露于热水中固化。Pexidan® R/T与加拿大标准协会一起列出,用于RW-90和RWU-90 XLPE应用,额定温度为-40°C。Pexidan® R/T符合RoHS。 Low density moisture curable polyethylene compound for low voltage building wire insulation (CSA RW-90, RWU-90, AC-90, TECK-90). PEXIDAN ® R/T is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a catalyst masterbatch CAT-009. Mixed in the proper proportions (95/5) the two components result in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN ® R/T is listed with the Canadian Standards Association for use in RW-90 and RWU-90 XLPE applications and rated to -40°C. PEXIDAN ® R/T is non-flame-retardant, halogen-free and RoHS-compliant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
72 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
12.4 | MPa | CSA 22.2 No. 38 |
断裂 fracture |
16.5 | MPa | CSA 22.2 No. 38 |
断裂 fracture 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | CSA 22.2 No. 38 | |
断裂 fracture 2 |
% | ASTM D638 | |
Shrinkback Shrinkback |
mm | CSA 22.2 No. 38 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
变形 deformation |
% | CSA 22.2 No. 38 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
60 Hz 60 Hz |
CSA 22.2 No. 38 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
绝缘电阻 insulation resistance |
CSA 22.2 No. 38 | ||
15℃ 15℃ |
Mohms/km | CSA 22.2 No. 38 | |
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/km | CSA 22.2 No. 38 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
高温伸长率 High temperature elongation 3 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 3 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 After thermal ageing (7days @121°C) |
3 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
聚乙烯塑料是乙烷加工消费的最终产品之一
2018-10-26 这个十月,在国际市场对于原油价格上涨的关注达到一个又一个高点时,美国的乙烷价格也冲上了4年来的一个高点,对于乙烷的需求似乎终于赶上了因为页岩气革命而带来的源源不断的乙烷供应量。 作为生产量最大的聚合物,聚乙烯塑料是乙烷加工生产的最终产品之一。 乙烷经裂解转化为乙烯后经过进一步加工,就会由原先无色无味的气体“变身”为各类塑料制品厂所需的PE颗粒料等产品,而这些塑料颗粒等产物由于生产时聚合方式、环境的不同会拥有不同的性能,而这决定了它们的不同的用途,有些可以成为 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |