Kraton D1162P是一种基于苯乙烯和异戊二烯的透明线性三嵌段共聚物,聚苯乙烯含量为43%。它由北美提供,其物理形式如下所示。Kraton D1162 PT-作为一种粉末状致密颗粒提供,Kraton D1162 P用作粘合剂、密封剂和涂层的配料。它也可以用作沥青或热塑性塑料的改性剂和化合物配方。 SABIC® HDPE F00952J resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00952J a good combination of easy extrusion and high melt strength with strong physical properties. Typical applications are thin films with excellent strength and rigidity. The material contains anti-oxidants. Typical applications SABIC® HDPE F00952J resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.050 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
9.5 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
15 | µm | |
弹性模量 Elastic modulus |
|||
TD,15 µm,吹塑薄膜 TD, 15 µ m, blow molded film |
1500 | MPa | ASTM D882 |
MD,15 µm,吹塑薄膜 MD, 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,15 µm,吹塑薄膜 MD, yield, 15 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,15 µm,吹塑薄膜 TD, yield, 15 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
15 µm,吹塑薄膜 15 µ m, blow molded film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:15 µm,吹塑薄膜 MD: 15 µ m, blow molded film |
g | ASTM D1922 | |
TD:15 µm,吹塑薄膜 TD: 15 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
常温可降解!韩国亚洲大学成功开发出了一种新的PBAT材料
2022-11-18 扫描上图二维码,可以免费下载 搜料 APP 近日, 韩国亚洲 大学李分烈教授、李平天教授团队成功 开发出了一种新的PBAT材料,可以在25摄氏度下降解。 科研团队将磷酸金属盐作为催化剂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |