| 牌号简介 About |
|---|
| Ultramid® 8272G HS BK-102 是一种12%的玻璃纤维增强、黑色颜料、热改性尼龙6吹塑复合材料，具有良好的工程性能和熔体强度的平衡，非常适合吹塑和其他需要超高熔体粘度的应用。 与标准吹塑等级相比，它具有更高的强度、刚度和抗蠕变能力。优异的渗透性和对油、碳氢化合物和大多数溶剂的耐化学性，以及优异的刚度和为低成本的金属替代品制造复杂形状的能力。 Ultramid 8272G HS BK102 is a 12% glass fiber reinforced, black pigmented, thermally modified, PA6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness ad the ability to fabricate complex shapes for cost effective metal replacements. Applications Ultramid 8272G HS BK102 is designed for blow molding applications requiring improved short term thermal performance as well as extrusions. It is ideal for air ducts, reservoirs and covers. |
产品描述 Product Description
厂家：德国巴斯夫 BASF Polyurethanes GmbH
类别：PA6 PA6
加工条件：注射成型 Injection Molding
性能特点： 低翘曲性; Low warping
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能
|
额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 密度 Specific Gravity | g/cm³ | ASTM D792 | |
| 密度 Density | g/cm³ | ISO 1183 | |
| 收缩率 收缩率 | |||
| MD：3.2 mm MD，3.18 mm | % | ||
| 吸水率 吸水率 | |||
| 饱和，23℃ 饱和，23℃ | % | ISO 62 | |
| 饱和 饱和 | % | ASTM D570 | |
| 平衡，23℃，50% RH 平衡，23℃，50% RH | % | ISO 62 | |
| 平衡，50% RH Equilibrium，50% RH | % | ASTM D570 | |
| 24hr 24 hr | % | ASTM D570 | |
| 23℃，24hr 23℃，24 hr | % | ISO 62 | |
|
冲击性能
|
额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 简支梁缺口冲击强度 简支梁缺口冲击强度 | |||
| 23℃ 23℃ | kJ/m² | ISO 179 | |
| 悬臂梁缺口冲击强度 Notched Izod Impact Strength | ASTM D256 | ||
| 23℃ 23℃ | kJ/m² | ISO 180 | |
| -40℃ -40°C | J/m | ASTM D256 | |
| 23℃ 23°C | J/m | ASTM D256 | |
|
热性能
|
额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 热变形温度 热变形温度 | |||
| 1.8 MPa，未退火 1.8 MPa，未退火 | ℃ | ASTM D648 | |
| 1.8 MPa，未退火 1.8 MPa，未退火 | ℃ | ISO 75-2/A | |
| 0.45 MPa，未退火 0.45 MPa，未退火 | ℃ | ISO 75-2/B | |
| 熔融峰值温度 Peak Melting Temperature | ℃ | ASTM D3418 | |
| 熔融温度 溶融温度 | |||
| DSC DSC | ℃ | ISO 3146 | |
| 线性热膨胀系数 线性热膨胀系数 | |||
| TD TD | 1/℃ | ||
| MD MD | 1/℃ | ||
| MD MD | 1/℃ | ASTM E831 | |
|
电气性能
|
额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 体积电阻率 Volume Resistivity | ohms·cm | IEC 60093 | |
| 1.50 mm 1.50 mm | ohms·cm | ASTM D257 | |
|
机械性能
|
额定值 Nominal Value | 单位 Units | 测试方法 Test Method |
| 拉伸模量 Tensile Modulus | ISO 527-2 | ||
| -40℃ -40°C | MPa | ISO 527-2 | |
| 23℃ 23°C | MPa | ISO 527-2 | |
| 80℃ 80°C | MPa | ISO 527-2 | |
| 120℃ 120°C | MPa | ISO 527-2 | |
| 150℃ 150°C | MPa | ISO 527-2 | |
| 拉伸强度 Tensile Strength | ASTM D638 | ||
| 断裂，-40℃ Break, -40°F | MPa | ASTM D638 | |
| 断裂，23℃ Break, 73°F | MPa | ASTM D638 | |
| 断裂，121℃ Break, 121°C | MPa | ASTM D638 | |
| 拉伸强度 Tensile Stress | ISO 527-2 | ||
| 断裂，-40℃ Break, -40°F | MPa | ISO 527-2 | |
| 断裂，23℃ Break, 73°F | MPa | ISO 527-2 | |
| 断裂，120℃ Break, 248°F | MPa | ISO 527-2 | |
| 断裂，150℃ Break, 302°F | MPa | ISO 527-2 | |
| 拉伸应变 Tensile Elongation | ASTM D638 | ||
| 断裂，-40℃ Break, -40°F | % | ASTM D638 | |
| 断裂，23℃ Break, 73°F | % | ASTM D638 | |
| 断裂，121℃ Break, 121°C | % | ASTM D638 | |
| 拉伸应变 Tensile Strain | ISO 527-2 | ||
| 断裂，-40℃ Break, -40°F | % | ISO 527-2 | |
| 断裂，23℃ Break, 73°F | % | ISO 527-2 | |
| 断裂，120℃ Break, 248°F | % | ISO 527-2 | |
| 断裂，150℃ Break, 302°F | % | ISO 527-2 | |
| 弯曲模量 Flexural Modulus | ASTM D790 | ||
| 23℃ 23℃ | MPa | ISO 178 | |
| -40℃ -40°C | MPa | ASTM D790 | |
| 23℃ 23°C | MPa | ASTM D790 | |
| 121℃ 121°C | MPa | ASTM D790 | |
| 弯曲强度 Flexural Strength | ASTM D790 | ||
| -40℃ -40°C | MPa | ASTM D790 | |
| 23℃ 23°C | MPa | ASTM D790 | |
| 121℃ 121°C | MPa | ASTM D790 | |
| 洛氏硬度 洛氏硬度 | |||
| R 级 R 级 | ASTM D785 | ||
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
东丽推出新型分离氢渗透膜组件
2022-03-06 近日，东丽工业公司宣布开发出一种新型高分子分离氢渗透膜组件。该膜组件将允许更有效地从混合气体中渗透分离出氢气。 东丽表示，公司利用反渗透膜培养技术，使用具有高氢浸润 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付