牌号简介 About |
---|
MVR(300°C/1.2 kg)7 cm / 10分钟;结构泡沫;5%玻璃纤维增强;阻燃;高粘度;易释放;注射成型;可用天然(不透明)和不透明颜色;结合适当发泡剂生产结构泡沫模塑制品 MVR (300 °C/1.2 kg) 7.0 cm³/10 min; structural foam; 5 % glass fiber reinforced; flame retardant; high viscosity; easy release; injection molding; available in natural (opaque) and opaque colors; in combination with an appropriate blowing agent for the production of structural foam moldings |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PC Polycarbonate
用途:结构泡沫;
颜色:不透明,可用颜色,自然色
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 含脱模剂; 高粘度; 阻燃; 防火阻燃等级5VA; High Viscosity,Good stripping performance,Flame Characteristics,V-0,5VA
填料:玻璃纤维 5
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ISO 1183 |
表观密度 Apparent density 2 |
0.65 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
8.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
7.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 3 |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
0.55 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
23℃,完全断裂 23 ℃, completely fractured 8 |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃,完全断裂 -60 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
-20℃,完全断裂 -20 ℃, completely fractured 9 |
kJ/m² | ISO 179/1eU | |
-20℃,完全断裂 -20 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured 9 |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 10 |
|||
23℃,完全断裂 23 ℃, completely fractured 10 |
kJ/m² | ISO 7391 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ISO 75-2/B | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火,6.0 mm 0.45 MPa, unannealed, 6.0 mm 4 |
℃ | ISO 75-2/B | |
热变形温度 Hot deformation temperature |
ISO 75-2/A | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火,6.00 mm 1.8 MPa, unannealed, 6.00 mm 4 |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
ISO 306/B50 | ||
B50 B50 11 |
℃ | ISO 306/B50 | |
B50 B50 |
℃ | ISO 306/B50 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient 12 |
|||
23℃ 23℃ 12 |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,3.00 mm Electrical performance, 3.00 mm |
℃ | UL 746 | |
强度机械性能,3.00 mm Strength mechanical performance, 3.00 mm |
℃ | UL 746 | |
冲击机械性能,3.00 mm Impact mechanical performance, 3.00 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
3.00 mm,灰色 3.00 mm, gray |
UL 94 | ||
6.00 mm,灰色 6.00 mm, gray 4 |
UL 94 | ||
5.00 mm,灰色 5.00 mm, gray |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
4.0 mm 4.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 13 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
23℃,6 mm 23℃,6 mm 4 |
MPa | ISO 527-2/25 | |
拉伸强度 tensile strength |
ISO 527-2/5 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/5 | |
断裂,23℃,6 mm Fracture, 23 ℃, 6 mm 4 |
MPa | ISO 527-2/5 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
ISO 527-2/5 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/5 | |
断裂,23℃,6 mm Fracture, 23 ℃, 6 mm 4 |
% | ISO 527-2/5 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 5 |
ISO 178 | ||
23℃,6 mm 23℃,6 mm 4 |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
3.50% 应变,23℃,6.00 mm 3.50% strain, 23 ℃, 6.00 mm 4 |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
23℃,6 mm 23℃,6 mm 4 |
MPa | ISO 178 | |
弯曲应变 Bending strain |
ISO 178 | ||
23℃ 23℃ 6 |
% | ISO 178 | |
23℃,6.00 mm 23℃,6.00 mm 7 |
% | ISO 178 | |
球压硬度 Ball hardness |
ISO 2039-1 | ||
-- -- |
MPa | ISO 2039-1 | |
6.00 mm 6.00 mm 4 |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 Foamed; density in the foamed state: 900 to 1000 kg/m³ |
5 0.079 in/min |
6 2 mm/min |
7 2 mm/min, Foamed; density in the foamed state: 900 to 1000 kg/m³ |
8 Based on ISO 179-1eA, 3 mm |
9 Foamed 6.0 mm; density in the foamed state: 900 to 1000 kg/m³ |
10 Based on ISO 180-A, 3 mm |
11 6.0 mm, Foamed; density in the foamed state: 900 to 1000 kg/m³ |
12 Cross-flow |
13 程序 A |
【新闻资讯】查看全部
国家能源局:上半年规上企业煤炭产量增长11%
2022-07-27 7月22日,国家能源局召开视频会议,持续推进煤炭生产供应,总结上半年煤炭生产供应形势,分析判断煤炭供需现状,研究部署进一步做好煤炭生产供应工作。 会议指出,上半年,全国 |
国家能源局:上半年规上企业煤炭产量增长11%
7月22日,国家能源局召开视频会议,持续推进煤炭生产供应,总结上半年煤炭生产供应形势,分析判断煤炭供需现状,研究部署进一步做好煤炭生产供应工作。
会议指出,上半年,全国规模以上企业煤炭产量21.94亿吨,同比增长11%,连续五个月保持两位数快速增长,推动电厂和港口储煤水平显著提高,煤炭增产保供成效显著。目前,稳定经济的措施带动了煤炭消费的持续增长。国际煤炭进口压力依然存在,煤炭生产和供应的增长不能放松。
会议要求,各单位要加强煤炭生产调度,协调解决增产保供问题,不折不扣地完成增产保供任务。要督促煤矿继续加大安全生产投入,提高安全管理保障能力。加快释放先进产能,确保煤炭产能持续平稳发展。加强对电煤中长期合同签订和履行的监督,确保量价落实到位。做好进口煤炭资源对接和合同签订工作,努力保持煤炭进口格局。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。