牌号简介 About |
---|
Ultraform® N 2320 003 UNC Q600是一种快速冷冻通用注塑POM级。它含有脱模剂。应用典型应用包括弹簧元件、夹子、气体加注口盖、齿轮、小型电机零件、窗帘钩和安全带释放按钮。 Ultraform N 2320 003 UNC Q600 is a rapidly freezing general-purpose injection-molding POM grade. It contains a mold release agent. Applications Typical applications include spring elements, clips, gas filler caps, gear wheels, small motor parts, curtain hooks and release buttons for safety belts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.40 | g/cm³ | ASTM D792 |
密度 Density |
1.40 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
7.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD:3.2 mm MD:3.2 mm |
2.0 | % | |
TD TD |
2.1 | % | ISO 294-4 |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,-40℃ Yield, -40 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,80℃ Yield, 80 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 2 |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.5 mm |
【新闻资讯】查看全部
从添加剂和工艺技术探求包装薄膜行业开展
2017-06-26 包装薄膜为满足包装对减量、可靠、负责任,以及个性化的需求,创新材料及工艺层出不穷。本文将从添加剂和工艺两方面对当前包装薄膜创新技术进展进行梳理,以期对您进行技术创新时提供参考。 创新添加剂 拉伸膜带来灵活、方便携带、可再密封等诸多便利,其中单口包装更被认为是打包的理想包装,但是它是不可回收的。不过,采用RETAIN™增容剂能够在保持薄膜出色的物理性能和光学性能的同时,让薄膜生产商循环利用阻隔性薄膜废料进行生产。 |
从添加剂和工艺技术探求包装薄膜行业开展 包装薄膜为考虑包装对减药、靠谱、承担责任,及其人性化的要求,自主创新原材料及加工工艺五花八门。文中将从添加剂和加工工艺双方应对当今包装薄膜自主创新技术性进度开展整理,以求对您开展技术革新时出示参照。 自主创新添加剂 拉伸缠绕膜产生灵便、便捷带上、可再密封性等众多便捷,在其中单口包装更被觉得是装包的理想化包装,可是它是不可回收的。但是,选用RETAIN™扩容剂可以在维持薄膜优异的工艺性能和电子光学特性的另外,让薄膜制造商循环利用高阻隔薄膜废弃物开展生产制造。 从添加剂和生产工艺研究包装薄膜行业发展 在包装原材料生产制造中添加收购料控制成本,推动环境保护是拉伸膜厂家发展趋势的聚焦点之一。AddWorks® PKG 902在提升流延膜、双重拉申聚丙稀薄膜(BOPP)和吹膜中再生颗粒成分的另外,可以保证产品品质和生产流水线的高效率和速率。根据应用高些成分的再生颗粒来取代聚丙稀(PP)或高压聚乙烯(PE)原材料,能够 让包装制造商节省很多的成本费,另外也出示了一种更具有可持续的包装解决方法。这类入料便捷、流通性好的特有商品可以为膜材出示高級其他苛化维护,避免不可控性的溶体流动性速度的上升及其TPE或黑色斑的产生。AddWorks PKG 902还能协助膜材制造商操纵膜材变黄。膜材艺术美和质量的提高能够 协助生产商打进高档膜材销售市场。除此之外,该商品根据提升对溶体流动性速度(MFR)的可靠性,能够 减少破膜的潜在性风险性,进而提升生产流水线的速度。 应用新式有机硅材料添加剂能够 协助包装制造商提升生产率,而且能在维持产品质量标准的另外,尽量减少薄膜终断。新式有机硅材料添加剂运用于密度低高压聚乙烯(LDPE/LLDPE)注塑薄膜,可明显降低髙速大批FFS包装实际操作的工作压力。 微发泡在包装上的运用 发泡包装有利于缓存、减脂,并产生隔热保温实际效果,他们也十分轻巧,耐溶剂浸蚀,可安全性食品类触碰,具备优异的成本效益。包装公司期待在降低包装原材料的另外,为货品和食品类在运送全过程中出示缓存和维护。 新一代密度低高压聚乙烯 (LDPE)发泡级别商品SABIC®LDPE 2102FC。它是一款出示快速成型技术的密度低高压聚乙烯发泡原材料,适用防御性包装运用,它也是该产品系列中第一款能为发泡商降低50%排气管存储時间(这代表着降低发泡商的库存量) 的商品,另外因为生产制造全过程中的废料越来越少和更优的一致性发泡特性,生产率也提升了5%。 北欧化工发布的Daploy HMS高溶体抗压强度聚丙稀泡沫塑料,因仅有一种单一材料,可100%可回收利用,不但可缓解净重,更具备隔热保温,应用溫度从-10℃ 到125℃,范畴较广,并具备与众不同的表层触感,适用包含货运物流包装和食品类、饮品服务项目以内的好几个行业。 德国巴斯夫的ecovio®发泡内肌泡沫塑料原材料,选用微生物原料,根据了可沤肥验证,尤其适用高使用价值或易破商品的运送包装。在这种运用场所,高质量的抗冲击特点和牢固性十分重要。 微发泡不但用在板塑胶板材上,在薄膜中也可选用微发泡技术。陶氏发布了一种微发泡批准转让技术,运用陶氏微发泡技术可根据物理学发泡减少共挤薄膜的相对密度(净重),那样就可以选用同量的环氧树脂生产制造大量的包装原材料。微孔板发泡技术融合陶氏的聚乙烯树脂系列产品,可改进包装的密闭性,降低包装的乱用;另外它还能造成多元化的电子光学特点,提升包装的股权溢价;它比传统式的包装,更具备环境保护性。微发泡包装轻巧灵便,是食品企业的理想化挑选。该技术性可运用于梳理热缩膜及其护肤品、环境卫生和清洁用品的软包装,另外可运用于立柱式袋及其复合型PE、PE PET、PE和BOPP薄膜中。别的的运用包含降低色浆负荷薄膜、FFS(添充、方式及密封性)包装、中重型运送袋、软包装袋和清洗袋等。 来源于:快塑见解 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。