牌号简介 About |
---|
Hostacom TSOP EM5 D63104是一种高流动、紫外线稳定、矿物填充的聚丙烯共聚物,具有高冲击性和良好的硬度。该等级的汽车已设计用于大型汽车应用,如仪表板和内饰。 Hostacom TSOP EM5 D63104 is a high flow, UV Stabilised, mineral filled polypropylene copolymer which exhibits high impact combined with excellent stiffness. The grade has been designed for large automotive applications such as instrument panels and interior trim. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
28 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
> 2.0 | kJ/m² | ISO 180-1A |
23℃ 23℃ |
> 20 | kJ/m² | ISO 180-1A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
57.0 | ℃ | ISO 75-2/A |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
Nordson新型塑化套装提高注塑成型高玻纤混合物产能
2017-09-25 Nordson的Xaloy塑化套装包含为高产量和低剪切混合,以及减少纤维断裂而设计的耐磨螺杆、料筒及阀门。 针对含有高水平玻璃纤维增强材料的聚合物的新型塑化系统提供耐磨性、高产能及温和混合,使得注塑厂商能够满足金属置换和其他高强度应用的要求,同时还能提高生产率和零部件质量。 据介绍,Xaloy高玻璃纤维填充聚合物塑化套装专为填充物含量自10%到60%不等的各种树脂注塑流程设计,将由 Nordson在Fakuma 2017上推出。 Xaloy塑 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |