Mitsui 三井 TPX共聚物 TPX® MBZ230(A)物性表,塑料价格,代理商,黄卡认证,MSDS,ROHS

牌号简介 About
TPX® MBZ230(A)是一种聚甲基戊烯共聚物（PMP 共聚物）材料,。该产品在北美洲有供货,加工方式为:挤出或注射成型。 TPX™ MBZ230(A) TPX™ MBZ230(A) is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion or injection molding. TPX™ MBZ230(A) TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware.

牌号简介 About

      TPX® MBZ230(A)是一种聚甲基戊烯共聚物（PMP 共聚物）材料,。该产品在北美洲有供货,加工方式为:挤出或注射成型。
         TPX™ MBZ230(A) TPX™ MBZ230(A) is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion or injection molding.
      TPX™ MBZ230(A) TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware.

技术参数 Technical Data
物理性能 PHYSICAL	额定值 Nominal Value	单位 Units	测试方法 Test Method
密度 Density	1.10	g/cm³	内部方法
熔体质量流动速率 Melt Flow Rate
260℃，5.0kg 260℃，5.0kg	57	g/10min	内部方法
螺旋流动长度 Spiral flow length ³	48.0	cm	内部方法
收缩率 Shrinkage ⁴			内部方法
MD：2.0 mm MD：2.0 mm	注册或登录后所有资料免费	%	内部方法
TD：2.0 mm TD：2.0 mm	注册或登录后所有资料免费	%	内部方法
吸水率 Water Absorption	注册或登录后所有资料免费
饱和 saturated	注册或登录后所有资料免费	%	ASTM D570
冲击性能 IMPACT	额定值 Nominal Value	单位 Units	测试方法 Test Method
悬臂梁缺口冲击强度 Izod Notched Impact strength	注册或登录后所有资料免费
注塑 Injection molding	注册或登录后所有资料免费	J/m	ASTM D256
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength ⁷	注册或登录后所有资料免费
23℃，注塑成型 23 ℃, injection molding ⁷	注册或登录后所有资料免费	J/m	ASTM D4812
热性能 THERMAL	额定值 Nominal Value	单位 Units	测试方法 Test Method
热变形温度 HDT ⁸	注册或登录后所有资料免费
0.45 MPa，未退火，6.35 mm 0.45 MPa, unannealed, 6.35 mm ⁸	注册或登录后所有资料免费	℃	ASTM D648
维卡软化温度 Vicat Softening Temperature	注册或登录后所有资料免费	℃	ASTM D1525 9
结晶峰温度 Crystallization peak temperature	注册或登录后所有资料免费
DSC DSC	注册或登录后所有资料免费	℃	ASTM D3418
线性热膨胀系数 Coeff.of linear therm expansion	注册或登录后所有资料免费
MD：-10~160℃ MD：-10~160℃	注册或登录后所有资料免费	1/℃	内部方法
电气性能 ELECTRICAL	额定值 Nominal Value	单位 Units	测试方法 Test Method
体积电阻率 Volume resistivity ¹⁰	注册或登录后所有资料免费
2 mm 2 mm ¹⁰	注册或登录后所有资料免费	ohms·cm	ASTM D257
介电强度 Dielectric strength ¹⁰	注册或登录后所有资料免费
2 mm 2 mm ¹⁰	注册或登录后所有资料免费	kV/mm	ASTM D149
介电常数 Dielectric constant ¹⁰	注册或登录后所有资料免费
2.00 mm，1 MHz 2.00 mm，1 MHz ¹⁰	注册或登录后所有资料免费		ASTM D150
机械性能 MECHANICAL	额定值 Nominal Value	单位 Units	测试方法 Test Method
洛氏硬度 Rockwell hardness	注册或登录后所有资料免费
R 级 R-level	注册或登录后所有资料免费		ASTM D785
拉伸模量 Tensile modulus ⁵	注册或登录后所有资料免费
23℃，注塑成型 23 ℃, injection molding ⁵	注册或登录后所有资料免费	MPa	ASTM D638
拉伸强度 tensile strength ⁵	注册或登录后所有资料免费		ASTM D638
屈服，23℃，注塑成型 Yield, 23 ℃, injection molding	注册或登录后所有资料免费	MPa	ASTM D638
断裂，23℃，注塑成型 Fracture, 23 ℃, injection molding	注册或登录后所有资料免费	MPa	ASTM D638
拉伸应变 Tensile strain ⁵	注册或登录后所有资料免费
断裂，23℃，注塑成型 Fracture, 23 ℃, injection molding ⁵	注册或登录后所有资料免费	%	ASTM D638
弯曲模量 Flexural Modulus ⁶	注册或登录后所有资料免费
3.20 mm，注塑成型，51 mm跨距 3.20 mm, injection molded, 51 mm span ⁶	注册或登录后所有资料免费	MPa	ASTM D790
弯曲强度 Flexural Strength ⁶	注册或登录后所有资料免费
3.20 mm，注塑成型，51 mm跨度 3.20 mm, injection molded, 51 mm span ⁶	注册或登录后所有资料免费	MPa	ASTM D790

技术参数 Technical Data

物理性能
PHYSICAL

额定值
Nominal Value

单位
Units

测试方法
Test Method

密度
Density

g/cm³

内部方法

熔体质量流动速率
Melt Flow Rate

260℃，5.0kg
260℃，5.0kg

g/10min

内部方法

螺旋流动长度
Spiral flow length ³

内部方法

收缩率
Shrinkage ⁴

内部方法

MD：2.0 mm
MD：2.0 mm

内部方法

TD：2.0 mm
TD：2.0 mm

内部方法

吸水率
Water Absorption

饱和
saturated

ASTM D570

冲击性能
IMPACT

额定值
Nominal Value

单位
Units

测试方法
Test Method

悬臂梁缺口冲击强度
Izod Notched Impact strength

注塑
Injection molding

J/m

ASTM D256

悬臂梁无缺口冲击强度
Izod Unnotched Impact strength ⁷

23℃，注塑成型
23 ℃, injection molding ⁷

J/m

ASTM D4812

热性能
THERMAL

额定值
Nominal Value

单位
Units

测试方法
Test Method

热变形温度
HDT ⁸

0.45 MPa，未退火，6.35 mm
0.45 MPa, unannealed, 6.35 mm ⁸

℃

ASTM D648

维卡软化温度
Vicat Softening Temperature

℃

ASTM D1525 9

结晶峰温度
Crystallization peak temperature

DSC
DSC

℃

ASTM D3418

线性热膨胀系数
Coeff.of linear therm expansion

MD：-10~160℃
MD：-10~160℃

1/℃

内部方法

电气性能
ELECTRICAL

额定值
Nominal Value

单位
Units

测试方法
Test Method

体积电阻率
Volume resistivity ¹⁰

2 mm
2 mm ¹⁰

ohms·cm

ASTM D257

介电强度
Dielectric strength ¹⁰

2 mm
2 mm ¹⁰

kV/mm

ASTM D149

介电常数
Dielectric constant ¹⁰

2.00 mm，1 MHz
2.00 mm，1 MHz ¹⁰

ASTM D150

机械性能
MECHANICAL

额定值
Nominal Value

单位
Units

测试方法
Test Method

洛氏硬度
Rockwell hardness

R 级
R-level

ASTM D785

拉伸模量
Tensile modulus ⁵

23℃，注塑成型
23 ℃, injection molding ⁵

MPa

ASTM D638

拉伸强度
tensile strength ⁵

ASTM D638

屈服，23℃，注塑成型
Yield, 23 ℃, injection molding

MPa

ASTM D638

断裂，23℃，注塑成型
Fracture, 23 ℃, injection molding

MPa

ASTM D638

拉伸应变
Tensile strain ⁵

断裂，23℃，注塑成型
Fracture, 23 ℃, injection molding ⁵

ASTM D638

弯曲模量
Flexural Modulus ⁶

3.20 mm，注塑成型，51 mm跨距
3.20 mm, injection molded, 51 mm span ⁶

MPa

ASTM D790

弯曲强度
Flexural Strength ⁶

3.20 mm，注塑成型，51 mm跨度
3.20 mm, injection molded, 51 mm span ⁶

MPa

ASTM D790

备注
1 一般属性：这些不能被视为规格。
2 模具温度: 163°F, 熔体温度: 590°F
3 260 to 280°C
4 类型 4, 2.0 in/min
5 0.051 in/min
6 Partial Break
7 120°C/hr
8 速率 A (50°C/h), 压力1 (10N)
9 Injection Molded

备注

1 一般属性：这些不能被视为规格。

2 模具温度: 163°F, 熔体温度: 590°F

3 260 to 280°C

4 类型 4, 2.0 in/min

5 0.051 in/min

6 Partial Break

7 120°C/hr

8 速率 A (50°C/h), 压力1 (10N)

9 Injection Molded

东方雨虹TPO助力4项工程入选“第十九届中国土木工程詹天佑奖”

近日，中国土木工程学会、北京詹天佑土木工程科学技术发展基金会正式公布第十九届中国土木工程詹天佑奖获奖名单。东方雨虹TPO以优质的产品性能与严苛的标准化施工，助力四项精品工程——“北京新机场工程（航站楼及换乘中心、停车楼）”“中国·红岛国际会议展览中心工程”“CEC·咸阳第8.6代薄膜晶体管液晶显示器件（TFT-LCD）项目”“上海浦东国际机场卫星厅及捷运系统工程”成功入选。

寰俊鍥剧墖_20220122102052.jpg

北京新机场工程（航站楼及换乘中心、停车楼）

北京新机场工程位于中国北京市大兴区榆垡镇、礼贤镇和河北省廊坊市广阳区之间，为4F级国际机场、世界级航空枢纽、国家发展新动力源*。2014年12月26日，北京新机场项目开工建设；2018年9月14日，北京新机场项目定名“北京大兴国际机场”。截至2021年2月，北京大兴国际机场航站楼面积为78万平方米；可满足2025年旅客吞吐量7200万人次、货邮吞吐量200万吨、飞机起降量62万架次的使用需求*。

寰俊鍥剧墖_20220122102103.jpg

北京新机场工程（航站楼及换乘中心、停车楼）主体屋面全部采用东方雨虹TPO防水卷材。

寰俊鍥剧墖_20220122102112.jpg

其中中央穹顶及指廊中线采用了玻璃天窗透光系统，天窗间的天沟采用外露的白色TPO高分子卷材作为防水系统直接承担所有的防水作用。东方雨虹TPO团队从设计初期就积极参与技术、施工配合及支持。

寰俊鎴
</td>
</tr>
</tbody>
</table>
<table>

</table>
</div>

<div class=

【免责声明】

加工方式

注射

单位制

料筒后部温度

°C

料筒中部温度

°C

料筒前部温度

°C

模具温度

°C

注塑压力

MPa

保压

MPa

挤出

单位制

料筒1区温度

°C

料筒2区温度

°C

料筒3区温度

°C

料筒4区温度

°C

接头温度

°C

口模温度

°C

电邮一份说明书

发送至：（多个地址，中间以逗号隔开）

备注：

电邮一份说明书

发送至：（多个邮件地址，中间以逗号隔开）

备注：

搜料服务热线

400-6700-720

分享到微信

每月充值前100名会员活动大礼包，更多优惠在等着你哦！

活动说明

TPX® MBZ230(A) 询价发货，点击联系客服
TPX共聚物 \| 日本三井
色号 NC 此色号对应颜色本型号/色号暂未建立色号系统，敬请期待！下询价单(非工作时间) 温馨提示：如指定型号不能换，我们可尽快报价；如接受同等性能国产替代，集团工厂【塑擎实业】可降本按需定制。详询谢工13926159974（电话微信同）

价格走势图

电邮一份说明书

发送至：（多个地址，中间以逗号隔开）

备注：

电邮一份说明书

发送至：（多个邮件地址，中间以逗号隔开）

备注：

搜料服务热线

400-6700-720

分享到微信

每月充值前100名会员活动大礼包，更多优惠在等着你哦！

活动说明