牌号简介 About |
---|
ALCUDIA CA-7220B是稳定的与HALS(无色),紫外线吸收剂和抗氧化剂。这些复合薄膜的主要性能是耐太阳辐射、透光性和保温性。用于温室和隧道覆盖的薄膜。200m厚度,1:2:1三层共挤薄膜,中间层为ALCUDIA CA-7421B,外层为ALCUDIA CA-7220B,在最大太阳辐射为160Kly的地理区域具有三年的寿命。如需更多信息,请联系技术援助和发展部或商业关注服务部。由于共挤结构的流变性能不同,各生产线的工艺条件应进行优化。 ALCUDIA® CA-7220B is stabilized with HALS (colourless), UV absorber and antioxidants. The main properties of these compound films are high solar radiation resistance, light transmission and heat retention. APLICATIONS Films for greenhouses and tunnels cover. 200 µm thickness, 1:2:1 three layers coextruded films, with ALCUDIA® CA-7421B in the middle layer and ALCUDIA® CA-7220B in the external layers, have a lifetime of the three years in geographical areas where maximum solar radiation is 160 Kly. For further information, contact to Technical Assistance and Development Department or Commercial Attention Service. Processing conditions should be optimized for each production line because of different rheological properties in coextruded structures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.928 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.40 | g/10min | ISO 1133 |
丁酯丙烯酸成分 Butyl acrylate composition |
3.0 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
200 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
22.0 | MPa | ISO 527-3 |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:200 µm,吹塑薄膜 MD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
TD:200 µm,吹塑薄膜 TD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
% | ASTM D1003 | |
Global Transmission of Visible Light(200.0 µm) Global Transmission of Visible Light(200.0 µm) 2 |
% | EN 13206 | |
IR Absorption(200.0 µm) IR Absorption(200.0 µm) 2 |
% | EN 13206 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
模具行业:如何分享两万亿的大市场?
2016-06-21 目前,积三十年改革开放之努力,中国已成为世界上最大的工业国家、最主要的工业产品输出地,同时亦是世界第二大经济体。中国的崛起,是进入二十一世纪二十年代以来世界经济版图中最主要的变化。然而,作为一个新近崛起的工业化国家,中国的工业规模虽大、能力虽强,但却还有着不少的制约因素。模具产业,则是其中主要的一项。 自上世纪末以来,随着发达国家的工业“空心化”政策,其模具制造重心向以中国为代表的发展中国家转移。同时,随着国内制造业的扩张,作为基础的模具制造产业也成长迅速。不过,随着二十余 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |