牌号简介 About |
---|
尿素-甲醛树脂,三聚氰胺树脂,以高度精制的纤维素为填料,并进一步用少量专用添加剂、颜料、固化调节剂和润滑剂进行改性。Urochem 134模塑料可以提供几乎无限的颜色范围,从半透明的轻粉到黑色。模件无异味,抗紫外线,防潮性能好。坚硬、光滑、耐刮擦的表面。优异的耐化学性。脂肪、油和常见的有机溶剂(如酒精和丙酮)不会侵蚀也能抵抗表面活性剂和弱碱的成型部件。它们能在较短的时间内抵抗弱酸的攻击。优异的电气性能(灭弧、跟踪、阻燃)。在不使用外部阻燃剂的情况下,氧气指数达到30%。成分中不存在卤素。符合广泛使用的氨基化合物材料规范的要求:BS 1322 UF A10(*)DIN 7708 131.5(*)ISO 2112 UF A10(*)UL认证(*)包括在ISO 14527应用领域:主要用于热固性注塑工艺。特别适用于插座、灯座和家用断路器等电气元件。 Urea- formaldehyde resins with melamine resin fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants. The Urochem 134 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black. Moulded parts are free from odour; UV stable with good moisture resistance. Hard, glossy and scratch resistant surface. Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration. Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition. Compliant with the requirements of widely used material specifications for amino compounds: BS 1322 type UF A10 (*) DIN 7708 type 131.5 (*) ISO 2112 type UF A10 (*) UL certified (*) included in ISO 14527 Fields of application: Optimized for use primarily in the thermoset injection moulding process. Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.50 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
-- -- |
0.80 到 1.0 | % | ISO 2577 |
-- -- 3 |
0.80 到 1.1 | % | ISO 2577 |
吸水率 Water absorption rate |
< 200.0 | mg | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
> 55.0 | MPa | ISO 527-2 |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
DIN 53483 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 4 |
℃ | IEC 707 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post-shrink |
3 180 sec |
【新闻资讯】查看全部
美瑞新材与鹤壁煤化工年产10万吨PBS可降解材料项目开工
2021-10-25 搜料网资讯: 10月11日美瑞新材发布公告称,10月9日美瑞新材料股份有限公司与河南能源化工集团鹤壁煤化工有限公司签订了《战略合作意向性协议》,双方拟在聚丁二酸丁二醇酯(简称 |
美瑞新材与鹤壁煤化工年产10万吨PBS可降解材料项目开工 搜料网资讯:10月11日美瑞新材发布公告称,10月9日美瑞新材料股份有限公司与河南能源化工集团鹤壁煤化工有限公司签订了《战略合作意向性协议》,双方拟在“聚丁二酸丁二醇酯(简称PBS)产品”领域开展合作。 根据意向性协议,美瑞新材将以约定的采购方式及价格(相关采购方式及价格由双方另行协商,并签署正式采购协议予以确定)向鹤壁煤化工采购合作项目所需的原材料,包括但不限于丁二酸酐、1,4-丁二醇等,并就合作项目在生产原料采购、行业信息共享、原材料生产技术开发等方面给予鹤壁煤化工支持。双方约定,将共同探讨携手合作PBS产品,不断提升产品品质和生产规模。 根据公告,美瑞新材经过多年自主技术开发,已具备PBS产品的合成技术。利用丁二酸酐和1,4-丁二醇为主要原料的工艺路线,已经经过了试验开发、小试及中试阶段,拟进一步工业化生产。鹤壁煤化工已建成年产60万吨甲醇、年产10万吨1,4-丁二醇和年产3000吨丁二酸酐等项目,具备原料产业优势。 美瑞新材表示,基于对可生物降解材料行业长期发展的看好,也基于公司掌握了PBS产品较为成熟的生产技术以及鹤壁煤化工的原料产业优势,PBS项目合作具备政策基础、市场基础、技术基础和原料供应基础。基于上述考虑,双方经过友好协商,计划在PBS产品相关领域缔结长期、稳定的合作伙伴关系,发挥双方公司在原料、研发、生产、渠道方面的协同优势,以期获得良好的社会效益和经济效益,为社会的可持续发展做出更大的贡献。 10月8日,河南能源化工集团鹤壁煤化工公司与美瑞新材料股份有限公司合资建设年产10万吨可降解塑料(PBS)项目举行开工仪式。 项目由双方合资成立的美瑞科技(河南)有限公司负责运营。2021年8月,美瑞科技(河南)有限公司成立,注册资本5亿元。由美瑞新材料与河南能源化工集团鹤壁煤化工发起成立,地址位于河南省鹤壁市宝山经济技术开发区煤化大道1号。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。