牌号简介 About |
---|
EMERGE™ PC/PET 9500CR高级树脂是一种聚碳酸酯混合物,具有优异的化学和阻燃性能。该等级设计用于医疗设备外壳和其他需要反复接触医院常用的各种清洁剂和消毒剂的应用。该等级具有良好的美观性和韧性。它的UL 94额定值为2.0 mm时的V0。主要特性:根据ISO 10993(第5和10部分)进行试验应用:医疗器械外壳或外壳 EMERGE™ PC/PET 9500CR Advanced Resin is a polycarbonate blend with excellent chemical and ignition resistance properties. This grade was designed for use in medical equipment housings and other applications that are subject to repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. It has a UL 94 rating of V0 at 2.0 mm. Main Characteristics: Tested under ISO 10993 (Parts 5 & 10) Applications: Medical device housings or enclosures |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
260℃,5.0kg 260℃,5.0kg |
10 | g/10min | ASTM D1238 |
265℃,5.0kg 265℃,5.0kg |
13 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
0.60 到 0.95 | % | ASTM D955 |
TD TD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
0℃,3.20 mm,注塑,Peak Energy 0 ℃, 3.20 mm, injection molded, Peak Energy |
J | ASTM D3763 | |
0℃,3.20 mm,注塑,Total Energy 0 ℃, 3.20 mm, injection molding, Total Energy |
J | ASTM D3763 | |
23℃,3.20 mm,注塑,Peak Energy 23 ℃, 3.20 mm, injection molded, Peak Energy |
J | ASTM D3763 | |
23℃,3.20 mm,注塑,总能量 23 ℃, 3.20 mm, injection molding, total energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~80℃ MD:-40~80℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm 7 |
UL 94 | ||
2.00 mm 2.00 mm 8 |
UL 94 | ||
2.50 mm 2.50 mm 9 |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
2.5 mm 2.5 mm |
℃ | IEC 60695-2-12 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus 3 |
|||
3.20 mm,注塑成型 3.20 mm, injection molded 3 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 4 |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 4 |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
|||
3.20 mm,注塑成型 3.20 mm, injection molded 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
|||
3.20 mm,注塑成型 3.20 mm, injection molded 5 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 2,0 in/min |
4 0,051 in/min |
5 标准 B (120°C/h), 压 力1 (10N) |
6 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
7 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
8 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions |
【新闻资讯】查看全部
中石化发布黄河流域生态保护和能源化工高质量发展专项规划
2022-01-20 搜料网资讯: 近日,中国石化发布黄河流域生态保护和能源化工高质量发展专项规划,提出到2025年在黄河流域基本建成节能节水型清洁能源高效供给基地,打造行业领先的绿色发展新标 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |