牌号简介 About |
---|
Santoprene TPV系列原厂家为埃克森美孚,现已被美国塞拉尼斯收购。
它是热塑性弹性体(TPE)系列中的一种软质、黑色、通用型热塑性硫化弹性体(T PV)。这种材料同时具有良好的物理性质和耐化学性,适用于广泛的领域。这一牌 号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型、挤出成型、 吹塑成型、热成型或真空成型设备上加工。这是一种聚烯烃基材料,可在生产过程 中进行回收利用。 A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
0.968 | g/cm³ | ASTM D792 |
密度 Density Density |
0.970 | g/cm³ | ISO 1183 |
耐候性 Weather resistance Weather resistance |
f1 | UL 746C | |
Detergent Resistance Detergent Resistance |
f4 | UL 2157 | |
Detergent Resistance Detergent Resistance |
f3 | UL 749 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
|||
TD,断裂 brk,23℃ TD, fracture BRK, 23 ℃ |
MPa | ASTM D412 | |
TD,断裂 brk,23℃ TD, fracture BRK, 23 ℃ |
MPa | ISO 37 | |
TD,100% 应变 strain,23℃ TD, 100% strain strain, 23 ℃ |
MPa | ISO 37 | |
TD,100% 应变 strain,23℃ TD, 100% strain strain, 23 ℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
TD,断裂 brk,23℃ TD, fracture BRK, 23 ℃ |
% | ISO 37 | |
TD,断裂 brk,23℃ TD, fracture BRK, 23 ℃ |
% | ASTM D412 | |
撕裂强度 tear strength Tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩永久变形 Compression Set |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩永久变形 Compression Set |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Brittle Temperature Brittle Temperature |
℃ | ASTM D746 | |
脆化温度 Brittle Temperature Brittle Temperature |
℃ | ISO 812 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能 elec Electrical performance Elec |
℃ | UL 746 | |
强度机械性能 str Strength mechanical performance str |
UL 746 | ||
1.0 mm 1.0 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 Change in Tensile Strength in Air Change in Tensile Strength in Air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air Change in Ultimate Elongation in Air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(150℃,168 hr) Change in Tensile Strain at Break in Air(150℃,168 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,150℃,168 hr) Change in Durometer Hardness in Air (150 ℃, 168 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 Change in Shore Hardness in Air Change in Shore Hardness in Air |
|||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
拉伸强度的变化率 Change in Tensile Strength Change in Tensile Strength |
ASTM D471 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ASTM D471 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
拉伸强度的变化率 Change in Tensile Strength Change in Tensile Strength |
ISO 1817 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ISO 1817 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
极限伸长率的变化率 Change in Ultimate Elongation Change in Ultimate Elongation |
ASTM D471 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ASTM D471 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Change in tensile stress during fracture Change in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ISO 1817 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
邵氏硬度的变化率 Change rate of Shore hardness Change rate of Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙酸中 Shore A, 23 ℃, 168 hr, in acetic acid |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在环己烷中 Shore A, 23 ℃, 168 hr, in cyclohexane |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在洗涤剂(汰渍)中,2.5% Shaw A, 23 ℃, 168 hr, in detergent (Tide), 2.5% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在异丙醇中 Shore A, 23 ℃, 168 hr, in isopropanol |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在甲基乙基酮中 Shore A, 23 ℃, 168 hr, in methyl ethyl ketone |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在三氯乙烯中 Shore A, 23 ℃, 168 hr, in trichloroethylene |
ASTM D471 | ||
邵氏 A,100℃,168 hr,在去离子水中 Shore A, 100 ℃, 168 hr, in deionized water |
ASTM D471 | ||
邵氏 A,100℃,168 hr,在IRM 903油中 Shaw A, 100 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,125℃,168 hr,在IRM 903油中 Shaw A, 125 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏硬度的变化率 Change rate of Shore hardness Change rate of Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙酸中 Shore A, 23 ℃, 168 hr, in acetic acid |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在环己烷中 Shore A, 23 ℃, 168 hr, in cyclohexane |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在洗涤剂(汰渍)中,2.5% Shaw A, 23 ℃, 168 hr, in detergent (Tide), 2.5% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在异丙醇中 Shore A, 23 ℃, 168 hr, in isopropanol |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在甲基乙基酮中 Shore A, 23 ℃, 168 hr, in methyl ethyl ketone |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在三氯乙烯中 Shore A, 23 ℃, 168 hr, in trichloroethylene |
ISO 1817 | ||
邵氏 A,100℃,168 hr,在去离子水中 Shore A, 100 ℃, 168 hr, in deionized water |
ISO 1817 | ||
邵氏 A,100℃,168 hr,在IRM 903油中 Shaw A, 100 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,125℃,168 hr,在IRM 903油中 Shaw A, 125 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
质量变化率 mass change fraction Mass change fraction |
ASTM D471 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ASTM D471 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
质量变化率 mass change fraction Mass change fraction |
ISO 1817 | ||
23.0℃,168 hr,in Methylethylketone 23.0℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23.0℃,168 hr,in Isopropyl Alcohol 23.0℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23.0℃,168 hr,in Trichloroethylene 23.0℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
23.0℃,168 hr,in Cyclohexane 23.0℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23.0℃,168 hr,in Ethanol,95% 23.0℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23.0℃,168 hr,in Hydrochloric Acid,10% 23.0℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23.0℃,168 hr,in Detergent(Tide),2.5% 23.0℃,168 hr,in Detergent(Tide),2.5% |
% | ISO 1817 | |
23.0℃,168 hr,in Sulfuric Acid,98% 23.0℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
23.0℃,168 hr,in Acetic Acid 23.0℃,168 hr,in Acetic Acid |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
体积变化 volume change Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
耐连续最高温度 Resistance to continuous maximum temperature Resistance to continuous maximum temperature |
|||
1008 hr 1008 hr |
℃ | SAE J2236 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric Strength Dielectric Strength |
|||
23 ℃,2 mm 23 ℃,2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23 ℃,1.98 mm 23 ℃,1.98 mm |
ASTM D150 | ||
23 ℃,1.98 mm 23 ℃,1.98 mm |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot Wire Ignition Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.0 mm 1.0 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
环保风暴没死,环保税和消费大反省或使中小企业暴毙!
2017-10-18 环保风暴挺过来的塑料人,革命尚未成功,同志仍需努力!接下来的2个大动作要来了,要顶住! 一.环保税于2018年元月1日起开征 尽管减税被有些人看做是不负责任的行为,但是最近,世界各国政府还是掀起了竞争性减税的高潮,力图减轻企业和国民负担,吸引资本流入,重塑经济的竞争力。 再过不到3个月,即从2018年元月1日起,中国的环保费即将进入开征,作为完 |
环保风暴没死,环保税和消费大反省或使中小企业暴毙! 环境保护飓风挺回来的塑胶人,改革并未取得成功,朋友仍需勤奋!下面的两个大动作要来了,要抵住!
一.环保税于2018年元月1日起征收 虽然降税被有的人看作是逃避责任的个人行为,可是近期,世界各地政府部门還是刮起了竞争降税的高潮迭起,试图缓解企业和人民压力,吸引住资产注入,重构经济发展的竞争能力。 再过不上3个月,即从2018年元月1日起,我国的环境保护费将要进到征收,做为彻底的地税新税收,各地区已经如火如荼制订环境保护缴税规范,迎来房地产税以后的滔滔新福财。 而各省市在缴税征收率上争相盲目攀比,勇争第一,缴税规范之高,税款之重,让众多企业望而却步、伐功矜能,环保税变成一头凶狠的怪物,已经吞食企业最终的盈利。 前不久,广东财政厅官网 、广东财政局和广东省生态环境保护厅协同公布《广东省大气污染物和水污染物环境保护税适用税额的决定(草案)征求意见稿》。自2018年1月1日起,广东空气污染物每环境污染剂量征缴环保税税款1.8元,水空气污染物每环境污染剂量征缴环保税税款2.8元。假如按此规范,喂养出栏率天龄120天的鸡,每只鸡要交8角钱的环保税…… 广东省的环境保护缴税规范在全部当地政府中处在一般水准,稍高于国家标准。北京、上海、天津、江苏、湖北等因为现阶段实行较高的排污费规范,是广东省的2-8倍。假如按均值5倍规范测算,在这种地区养一只120天出栏率的鸡,征缴的环保税会做到4元…… 针对养殖场而言,它是一笔底部放量的支出,针对企业中小型企业而言,照此规范征缴的环保税也是一笔极大的压力。 依照这一发展趋势发展趋势下来,环保税彻底具有取代土地出让,变成当地政府较大 收益来源于的发展潜力。将来必定是土地财政向环境保护、诊疗财政局的迁移,方向是不容易变的。 在高厂租、高人力和高原料成本费的挤压成型下,环保税变成增税的马前卒,已经变成击垮中小型企业的麦草。在环境保护飓风中心存侥幸逃离,沒有停业整顿的中小型企业,极很有可能被即将来临的环保税推塔,并在未来环保税的棒子下突然死亡,这类几率已经大幅度升高。 不增税?地方公务员的刚度开支究竟是从哪里而来的呢??地方债务怎样市场出清?财政赤字怎样填补?
二.全国各地安全生产大检查回头巡视10月中下旬起动 10月13日,国务院安委办召开工作会议,对进行安全生产大检查“回头巡视”开展动员部署。国务院安委办办公室主任、我国安全管理质监总局副局孙华山列席会议并发言。 依照国务院安全委员会布署,“回头巡视”是安全生产大检查第三阶段重点工作,自10月中下旬起动,至10月底完毕,遮盖重特大大会整个过程。国务院安委办将机构创立31个检查组,深层次全国各地32个省级统计分析企业检查。 新闻记者从上海安全生产监督获知,依据国务院安全委员会和市人民政府部署工作,上海安监局已进行安全生产大检查工作中3个多月,关键聚焦点道路运输、度假旅游、建筑工程施工、消防安全、燃气管道、危化品、冶金工业、高层住宅房屋、人员密集场地、烟尘防爆型等关键行业领域,进一步增加安全生产大检查工作成效,机构了安全生产安全隐患专项检查、整顿。 截止10月16日,大检查获得了分阶段成果,共对57431家企业检查99200次,发觉安全风险61576项,催促企业按时进行整顿59870项,整顿率是97.23%,其他安全隐患已经井然有序落实整改中;对647家企业执行行政许可2707.36万余元。 大检查共严厉打击比较严重违反规定违规操作264起,关掉依法取缔企业1748家,停工整治951家,处罚13514.88万余元,追责刑事处罚372人,责任追究曝出工作中不到位企业163家、工作人员31人。 来源于:互联网技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
加工方式 | |||
---|---|---|---|
注塑成型 Injection Molding | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
最大含水量 Maximum Moisture Content | % | ||
最大回料比 Maximum return ratio | % | ||
后段温度 Rear Temperature -Zone 1 | °C | ||
中段温度 Middle Temperature -Zone 2 | °C | ||
前段温度 Front Temperature -Zone 3 | °C | ||
喷嘴温度 Nozzle Temperature | °C | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Mold Temperature | °C | ||
注射速度 Injection speed | |||
背压 Back Pressure | MPa | ||
螺杆转速 Screw Speed | rpm | ||
锁模力 clamping force | kN/cm² | ||
垫层 cushion | mm | ||
螺杆长径比 Draw Ratio of Screw | |||
螺杆压缩比 Screw Compression Ratio | |||
排气孔深度 Exhaust hole depth | mm | ||
挤出成型 Extrusion Molded | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
熔体温度 Melt Temperature | °C | ||
模头温度 Die Temperature | °C | ||
背压 Back pressure | MPa |