| 牌号简介 About |
|---|
| Viton® A-401C氟弹性体是一种结合固化的“A族”二聚体，设计用于密封装置的压缩成型，必须满足特定的氟弹性体规范。除了维顿氟弹性体的典型耐热和耐化学特性外，Viton® A-401C在加工和流变学方面提供了显著的改进。Viton® A-401C可以与类似的Viton类型混合，以提供加工、性能和收缩率的变化。与维顿E-60C相比，Viton® A-401C的特点：完全预组装的O形环固化水平改进压缩成型增加模具流动更容易脱模少结垢改进挤出提高固化率改进压缩定型阻力相同模具收缩维顿E-60C应用9527被高度推荐用于O形环挤压线、垫圈、密封件和型材。可配制Viton® A-401C以满足氟弹性体规范MIL-R-83248B、AMS 7276D和AMS 7259A。 Viton® A-401C fluoroelastomer is an incorporated cure "A-family" dipolymer designed for compression molding of sealing devices that must meet specific fluoroelastomer specifications. In addition to the heat and chemical resistance characteristics typical of Viton® fluoroelastomers, Viton® A-401C offers significant improvements in processing and rheology. Viton® A-401C can be blended with similar Viton® types to provide variations in processing, properties, and shrinkage. Features Compared with Viton® E-60C, Viton® A-401C features: Fully precompounded O-ring curative level Improved compression molding increased mold flow easier mold release less mold fouling Improved extrusion Increased cure rate Improved compression set resistance Same mold shrinkage as Viton® E-60C Applications Viton® A-401C is highly recommended for O-rings, extruded cord, gaskets, seals, and profiles. Viton® A-401C can be formulated to meet fluoroelastomer specifications Mil-R-83248B, AMS 7276D, and AMS 7259A. |
产品描述 Product Description
用途：管道;密封件;型材;垫圈;管件;
颜色：白色
加工条件：挤出 Extrusion
性能特点： 尺寸稳定性好; 含脱模剂; 耐化学性; 耐高温; 易流动; 易加工; Excellent Processability,Good Dimensional Stability,Good liquidity,Good stripping performance,High Heat Resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.82 | g/cm³ | ASTM D792 |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10，121℃ ML 1+10，121℃ |
80 | MU | ASTM D1646 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ |
74 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 2 |
78 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 3 |
76 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 4 |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变，23℃ 100% strain, 23 ℃ 6 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 7 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 8 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服，23℃ Yield, 23 ℃ 6 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 7 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 8 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂，23℃ Fracture, 23 ℃ 6 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 7 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 8 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
|
压缩形变 Compression deformation |
ASTM D395B | ||
|
23℃，70 hr 23℃，70 hr |
% | ASTM D395B | |
|
200℃，70 hr 200℃，70 hr |
% | ASTM D395B | |
|
200℃，168 hr 200℃，168 hr |
% | ASTM D395B | |
|
200℃，336 hr 200℃，336 hr |
% | ASTM D395B | |
|
232℃，70 hr 232℃，70 hr |
% | ASTM D395B | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 20 in/min |
| 3 20 in/min, 老化 70 hr 在 392°F |
| 4 20 in/min, 老化 168 hr 在 392°F |
| 5 20 in/min, 老化 24 hr 在 450°F |
| 6 20 in/min, 老化 70 hr 在 450°F |
| 7 老化 70 hr 在 392°F |
| 8 老化 168 hr 在 392°F |
| 9 老化 24 hr 在 450°F |
| 10 老化 70 hr 在 450°F |
|
【新闻资讯】查看全部 
迎战疫情，苏州重磅出台支持中小企业共渡难关的十条政策！
2020-02-04 苏州市人民政府关于应对 新型冠状病毒感染的肺炎疫情 支持中小企业共渡难关的 十条政策意见 各市、区人民政府，苏州工业园区、苏州高新区、太仓港口管委会； 市各有关部门和单 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付