EGDA-6888是一种高分子量、高密度聚乙烯共聚物,专为管状薄膜挤出而设计。其广泛的分子量分布和密度已得到优化,以提供良好的气泡稳定性在高挤出率和高薄膜强度和刚性。结合高强度和良好的下拉性能,使EGDA-6888在许多应用中的下降测量的理想选择。建议将EGDA-6888生产的管状薄膜用于高强度食品袋、购物袋、生产袋以及用于多壁袋衬里和薄纸产品替代品的高质量薄膜。薄膜几乎无凝胶,具有优良的可处理性。它们非常适合打印高质量的图形。 EGDA-6888 is a high molecular weight, high density polyethylene copolymer that has been designed specifically for tubular film extrusion. Its broad molecular weight distribution and density have been optimized to give excellent bubble stability at high extrusion rates with high film strength and rigidity. The combination of high strength and excellent drawdownability makes EGDA-6888 ideal for down gauging in many applications. Tubular films produced from EGDA-6888 are recommended for high strength grocery sacks, shopping bags, produce bags and high quality thin films for multiwall sack liners and replacements for thin paper products. Films are nearly gel-free and have excellent treatability. They are ideally suited for printing of high quality graphics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ASTM D792 |
体积密度 bulk density |
560 | kg/m³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
10 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
15 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:15 µm,吹塑薄膜 1% secant, MD: 15 µ m, blow molded film |
1220 | MPa | ASTM D882 |
1% 正割,TD:15 µm,吹塑薄膜 1% secant, TD: 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,15 µm,吹塑薄膜 MD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,15 µm,吹塑薄膜 TD, fracture, 15 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
15 µm,吹塑薄膜 15 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
ASTM D1922 | ||
MD,15 µm MD,15 µm |
kN/m | ASTM D1922 | |
TD,15 µm TD,15 µm |
kN/m | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陶氏PacXpert软包装技术在日本签署第二个受权协议
2015-12-14 陶氏化学旗下陶氏包装与特种塑料业务部宣布,近日与Takigawa公司签订了PacXpert软包装技术在日本的第二个授权协议,后者将通过其日本和越南两个生产基地,向亚太区多个行业的客户提供包装产品。 |
陶氏PacXpert软包装技术在日本签署第二个受权协议 陶氏有机化学集团旗下陶氏包裝与特种塑料市场部公布,近日与Takigawa企业签署了PacXpert软包装技术在日本的第二个授权协议,后面一种将根据其日本和越南地区2个生产制造产业基地,向亚太区好几个领域的顾客出示包裝商品。 陶氏与Takigawa企业宣布签署PacXpert软包装技术在日本的应用授权协议 Takigawa企业是日本领跑的软包装生产商,着眼于为不一样领域出示食品类和非食用具,固态与液體皆适合的高档包裝。本次签定授权协议后,Takigawa企业将根据其分销商互联网,把陶氏PacXpert软包装技术引向加拿大、印尼、日本、泰国的和越南地区销售市场,进一步增加这一技术在亚太区的知名度。 “大家十分希望将PacXpert软包装技术送到亚太区的每个地区。日本销售市场针对软包装的规范极高。可以一年本质日本成功签定2个授权协议是对PacXpert技术的较大 毫无疑问,也再一次证实了这是一个对顾客十分有使用价值的自主创新解决方法。日本软包装领域稳步增长,包装标准和要求拥有 显着提高。”陶氏包裝与特种塑料市场部亚太区商务接待高级副总裁麦索睿(Mark Saurin)讲到。 “做为自主创新包裝解决方法,PacXpert软包装技术有着许多与众不同的优势,例如对可持续发展观的奉献,及其考虑终端产品用户针对便捷易乱倒的规定。根据与陶氏协作,大家彼此能携手并肩开发产品,充分发挥协同作用,能够更好地扩展彼此在全世界的业务流程。” Takigawa公司老总Hiroyuki Takigawa点评道。 伴随着与Takigawa的协作落下帷幕,陶氏现阶段已在全世界范畴内签定了十一份PacXpert软包装技术的授权协议,在亚太区现有三家,包含于上年11月达到授权协议的日本一同包装印刷(Kyodo Printing)。 PacXpert软包装技术是一个轻巧型的产品包装设计,此技术选用迎合密封及其依照人体工学基本原理设计方案的经久耐用双手柄,可完成无渗漏精准乱倒,在闲置时,包装袋子可呈平扁状,贮运便捷。虽然是软包装,PacXpert能牢固地放置仓储货架上,既可站立置放,在添充后也可以侧边置放,有利于生产商将大中型硬质的塑料制品变换为携带式的软包装。除此之外,PacXpert技术还十分环境保护,能合理防止包裝內容物的消耗,降低原料耗费,并提升商品-包裝比例。 来源于:雅式橡塑制品网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。