牌号简介 About |
---|
木粉增强苯酚改性三聚氰胺模塑料具有优异的表面硬度、良好的机械性能、良好的电气性能、良好的耐热性,主要用途:电气工程中的模件、家用电器的安装件、汽车烟灰缸。本产品满足重金属和PCA,也符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)标识的要求,符合ISO 14528-1:MP(WD30+MD15)-(WD40+MD05)DIN 7708:MP 180 Wood flour reinforced phenol-modified Melamine moulding compound Excellent surface hardness, good mechanical properties, good electrical properties, good heat resistance Primary application(s): Moulded parts in electrical engineering, mountings for household appliances, car ashtrays This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 14528-1: MP (WD30+MD15) - (WD40+MD05) DIN 7708: MP 180 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.50 到 1.60 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.55 到 0.75 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
MD MD 3 |
0.80 到 1.2 | % | ISO 2577 |
MD MD 4 |
0.50 到 0.90 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 2.0 | % | ISO 62 |
后收缩 Post contraction 5 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eA | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eU | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
<50 h <50 h |
℃ | IEC 60216 | |
20,000 h 20,000 h |
℃ | IEC 60216 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 Injection Molded |
4 168 h / 110°C |
【新闻资讯】查看全部
难以相信:8 万公吨的塑料堆积在“泛大西洋渣滓带”
2018-03-26 根据一项新的科学估计,在加利福尼亚和夏威夷之间,有将近 8 万公吨的塑料存在于“泛大西洋垃圾带”里,国际研究人员指出,这个数字已是之前报道的 16 倍。 人们将一个拖网放置在这个垃圾带的中央,发现这个拖网上的塑料浓度创下了历史新高。塑料垃圾主要聚集在五个海洋区域,其中“泛大西洋垃圾带”是区域最大的一块。 |
难以相信:8 万公吨的塑料堆积在“泛大西洋渣滓带” 根据一项新的科学估计,在加利福尼亚和夏威夷之间,有将近 8 万公吨的塑料存在于“泛大西洋垃圾带”里,国际研究人员指出,这个数字已是之前报道的 16 倍。 人们将一个拖网放置在这个垃圾带的中央,发现这个拖网上的塑料浓度创下了历史新高。塑料垃圾主要聚集在五个海洋区域,其中“泛大西洋垃圾带”是区域最大的一块。 塑料垃圾在海洋的分布图 这项为期三年的测绘工作表明,塑料污染“以比周围的水流更快的速度呈指数增长”。在 160 万平方公里的海域里面,微塑料(能够严重影响鱼类幼体的生长发育、直径小于 5 毫米的塑料微粒)占漂浮的塑料总量的 8 % 。据估计,这块区域里有 1.8 万亿个塑料,其中一些比微塑料大的,包括了渔网、玩具甚至马桶盖。 来自荷兰 Utrecht 大学的 Erik van Sebille 与这个研究毫不相关,但当她得知这些数字后,用了“难以置信”一词来形容。这个项目同时也证明了:泛大西洋垃圾带向四周移动的速度超乎所有人的想象。 航空调查和船只的使用,是解释为什么预测值比过去高的一部分原因。除此之外,这些差异也可能归因于自以前的研究开展以来,塑料污染水平的上升。 这项发表在科学报告中的报告发现了以下内容: 1、在这部分海洋中,塑料占所有碎片的 99.9%。 2、至少有 46% 的塑料由渔网组成,超过四分之三的塑料是大于 5 厘米的碎片,包括硬塑料,塑料片和薄膜等。 3、尽管大多数大件物品已经分解成碎片,但研究人员能够识别出少量物品,包括容器、瓶子、盖子、包装带、绳索和渔网。 4、样本中有 50 个物品有可读的生产日期: 1977 年一个, 1980 年代七个, 1990 年代 17 个, 2000 年代 24 个,2010 年一个。 5、只有某些厚度足以浮起的碎片会滞留并积聚在该区域,例如用于包装的普通塑料聚乙烯和聚丙烯。 每年,都有数百万吨的塑料进入海洋。一些漂流到称为“环流”的循环的洋流的大系统中,塑料一旦被困在环流圈里,就会分解成微塑料,可能被海洋生物摄取。 研究所表明的信息很清楚,海洋环境专家 Laurent Lebreton 说:“它让我们回归到如何使用塑料。我们离不开塑料――我认为它在医学,运输和建筑中非常有用,但我认为我们必须改变我们使用塑料的方式,特别是在一次性塑料和那些使用寿命很短的塑料用品上。” 来源:好奇心日报 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。