牌号简介 About |
---|
Radel® R-5000是一种透明的聚苯砜(PPSU),具有优异的水解稳定性和韧性,优于其他商用高温工程树脂。该树脂还提供高偏转温度和优异的抗环境应力开裂性能。Radel聚合物具有固有的阻燃性,具有优异的热稳定性和良好的电气性能。烟雾:Radel® R-5000 cl 301琥珀色:Radel® R-5000 nt蓝色:Radel® R-5000 tr bu391 Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Smoke: Radel® R-5000 CL 301 Amber: Radel® R-5000 NT Blue: Radel® R-5000 TR BU391 |
产品描述 Product Description
厂家:比利时索尔维 Solvay
类别:PPSU
用途:牙齿应用领域;医疗/护理用品;膜;汽车领域的应用;医疗器械;外科器械;医疗器材;食品服务领域;
颜色:清晰/透明
加工条件:注射成型,薄膜挤出,吹塑成型,机器加工,热成型,片材挤出成型,型材挤出成型 Injection Molding,Film extrusion,Extrusion,Thermo forming,Profile extrusion
性能特点: 蒸汽消毒; 放射线可穿透; 辐射消毒; 电气性好; 耐老化; 尺寸稳定性好; 耐酸; 易消毒; 超高韧性; 生物兼容性; 环氧乙烷消毒; 电子束消毒; 防火阻燃等级V-0; 耐化学性; 阻燃; 抗应力开裂; 耐碱; 耐洗涤剂; 加热消毒; 热稳定性好; 高压灭菌器消毒; 抗伽马射线; 耐高温; 耐水解; 耐蒸汽; Gamma radiation,High Heat Resistance,Radiation disinfection,Heat Stabilized,Solvent resistance,Flame Characteristics,Good Electrical Properties,Ultra high toughness,Good Dimensional Stability,Hydrolysis stability,Radioactive,Steam sterilized,High ESCR,Ethylene oxide disinfection,Good heat aging resistance,E-beam disinfection,Good disinfection,Resistance to the steam,Biocompatible,Heat sterilization,Resistance to detergents,V-0,High pressure disinfection,Acidproof,Alkali resistant
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.29 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
365℃,5.0kg 365℃,5.0kg |
14 to 20 | g/10min | ASTM D1238 |
收缩率 Shrinkage Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.70 | % | ASTM D955 |
吸水率 Water Absorption Water Absorption |
|||
平衡 Equilibrium Balancing Equilibrium |
1.1 | % | ASTM D570 |
24hr 24hr |
0.37 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,3.18 mm Broken BRK, 3.18 mm |
% | ASTM D638 | |
屈服 yld,3.18 mm Yield yld, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
5% 应变,3.18 mm 5% strain, 3.18 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
拉伸冲击强度 Tensile Impact Strength Tensile Impact Strength |
|||
3.18 mm 3.18 mm |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ASTM E1356 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
ASTM D149 | ||
0.0254 mm 0.0254 mm |
kV/mm | ASTM D149 | |
3.18 mm 3.18 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
3.18 mm,60 Hz 3.18 mm,60 Hz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.76 mm 0.76 mm |
UL 94 | ||
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive Index Refractive Index |
ASTM D542 | ||
补充信息 Additional Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Steam Sterilization(w/ Morpholine) Steam Sterilization(w/ Morpholine) |
Cycles |
备注 |
---|
1 NSF STD-51 compliant for NT only. |
2 Tested at 82 °C (180 °F) (Commercial Hot) |
3 一般属性:这些不能被视为规格。 |
4 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
5 周期完成,无开裂、裂纹或破裂。 蒸气消毒条件: - 温度:270 °F(132 °C) - 时间: 30分钟/周期 - 蒸汽压力: 27 PSIG (0.19兆帕) -应力水平:弯曲1000 psi (7.0兆帕) - 添加剂:50 ppm吗啉 |
【新闻资讯】查看全部 |
镇海炼化乙烯气体裂解炉添加至12台 1月14日,中国较大 乙烯汽体裂解炉在镇海炼化打火烘炉,该炉生产量为15万吨级/年。到此,该公司乙烯裂解炉提升至12台。 来源于:生意社 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
加工方式 | |||
---|---|---|---|
注塑成型 Injection Molding | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Mold Temperature | °C | ||
螺杆压缩比 Screw Compression Ratio | |||
挤出成型 Extrusion Molded | Nominal Value | Unit | |
干燥温度 Drying Temperature | °C | ||
干燥时间 Drying Time | hr | ||
料筒-1区温度 Barrel - Zone 1 Temperature | °C | ||
料筒-2区温度 Barrel - Zone 2 Temperature | °C | ||
料筒-3区温度 Barrel - Zone 3 Temperature | °C | ||
料筒-4区温度 Barrel - Zone 4 Temperature | °C | ||
料筒-5区温度 Barrel - Zone 5 Temperature | °C | ||
适配器温度 Adapter Temperature | °C | ||
熔体温度 Melt Temperature | °C | ||
模具温度 Die Temperature | °C |