牌号简介 About |
---|
Softflex® 0470适用于ABS、PC、ABS/PC和PPO的二次成型。 Softflex 0470 is suitable for overmolding ABS, PC, ABS/PC and PPO. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.970 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
235℃,1.0kg 235℃,1.0kg |
1.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD:3.2 mm MD:3.2 mm |
1.6 到 3.3 | % | ASTM D955 |
TD:3.2 mm TD:3.2 mm |
1.7 到 2.9 | % | ASTM D955 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸永久变形 Tensile permanent deformation |
|||
100% 应变 100% strain |
105 | % | ASTM D412 |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield |
MPa | ASTM D412 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
|||
23℃ 23℃ |
% | ASTM D395 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
-30℃ -30℃ |
J | ASTM D5420 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 A,10 秒 Shore A, 10 seconds |
ASTM D2240 | ||
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-22 转轮 1000 cycles, 1000 g, H-22 wheels |
mg | ASTM D3389 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
改善吹塑件壁厚均匀性的几种方法
2016-08-23 1.异型口模 口模异型化是指挤出机头的口模或芯棒局部位置开设凹槽,增大对应制件拐角处的口模间隙,以增加型坯局部位置的壁厚,得到异型化的型坯,弥补吹胀比不一致造成的径向壁厚不均,从而得到壁厚较为均匀的制件。针对性地采用异型口模,并通过多次试模、优化、设计加工出合理的异型口模,可以极大提高制件壁厚分布的均匀性。 2.轴向壁厚控制技术 轴向壁厚控制技术的作用是使得挤出的塑料型坯,根 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |