牌号简介 About |
---|
普兰特科技有限公司开发和生产先进的生物基材料。Plantic是一种由玉米淀粉(玉米)制成的创新产品,由澳大利亚种植和非转基因玉米制成。Plantic是Plantic Technologies Limited在澳大利亚的注册商标。Plantic® R1是一种先进的技术表,由玉米淀粉制成,完全可生物降解和堆肥。Plantic® R1适用于热成型应用(例如,用于包装水活性为35%至70%的食品和货物)。也适用于直接接触高脂肪食物。 Plantic Technologies Limited develops and produces advanced bio-based materials. Plantic® is an innovative product made from corn-starch (maize) that is Australian grown and non-genetically modified. Plantic® is an Australian registered trademark of Plantic Technologies Limited. Plantic® R1 is an advanced technology sheet manufactured from corn starch that is fully biodegradable and compostable. Plantic® R1 is suitable for thermoforming applications (e.g. for packing foods & goods with water activity of 35% to 70%). Also suitable for direct contact with fatty foods. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 到 1.45 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
1.0 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
0.17 | ASTM D1894 | |
与自身 - 静态 With oneself - static |
0.22 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
250 | µm | |
割线模量 Secant modulus |
|||
MD,250 µm MD,250 µm |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
MD,屈服,250 µm MD, yield, 250 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
MD,断裂,250 µm MD, fracture, 250 µ m |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,250 µm MD,250 µm |
g | ASTM D1922 | |
透氧率 Oxygen permeability 2 |
|||
38℃,250 µm 38℃,250 µm 2 |
cm³/m²/24 hr | ASTM D1434 | |
水蒸气透过性 Water vapor permeability 3 |
g/m²/24 hr | ASTM E96 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM E1356 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,250 µm 60°,250 µm |
ASTM D2457 | ||
透光率 Transmittance |
|||
250 µm 250 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
250 µm 250 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Water Activity Water Activity 4 |
内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 50%RH |
3 38°C, 50%RH |
4 PTM 03 |
【新闻资讯】查看全部
2014年中国橡塑制品业研讨实验经费同比增长14.2%
2015-11-26 日前,中国国家统计局、科学技术部、财政部联合发布了《2014年全国科技经费投入统计公报》。公报显示,中国科技经费投入继续增长,国家财政科技支出及研究与试验发展(R&D)经费投入增加,研究与试验发展经费投入强度提高。 统计显示,2014年中国共投入研究与试验发展经费13015.6亿元,比上年增加1169.0亿元,增长9.9%;研究与试验发展经费投入强度(与国内生产总值之比)为2.05%,比上年提高0.04个百分点。按研究与试验发展人员(全时工作量)计算的人均经费支出为 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |