牌号简介 About |
---|
木粉增强苯酚改性三聚氰胺模塑料与MP 180相比,尺寸稳定性和电气性能得到改善,表面硬度优异,机械强度和耐热性良好,在电气工程中,该产品满足重金属和PCA的允许上限,并符合根据ISO 14529-1:MP(WD35+MD15)-(WD45+MD05)DIN 7708:MP 182,欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)标识的要求 Wood flour reinforced phenol-modified Melamine moulding compound Improved dimensional stability and electrical properties compared to MP 180, excellent surface hardness, good mechanical strength and heat resistance Moulded parts in electrical engineering This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) Identification according to ISO 14529-1: MP (WD35+MD15) -(WD45+MD05) DIN 7708: MP 182 |
产品描述 Product Description
厂家:美国拉西格 RASCHIG
类别:三聚氰胺酚醛 三聚氰胺酚醛
用途:电气元件;
加工条件:注射成型 Injection Molding
性能特点: 耐热性好; 防火阻燃等级V-0; 机械强度好; 硬度高; Good Rigidity,Good Hardness,Heat Resistance, Good,V-0
填料:有机填料
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 到 1.70 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.55 到 0.75 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
MD MD 3 |
0.70 到 1.1 | % | ISO 2577 |
MD MD 4 |
0.40 到 0.80 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 2.0 | % | ISO 62 |
后收缩 Post contraction 5 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
模压成型 Compression Molding |
MPa | ISO 178 | |
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eA | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eU | |
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
最高使用温度 Maximum operating temperature |
IEC 60216 | ||
<50 h <50 h |
℃ | IEC 60216 | |
20,000 h 20,000 h |
℃ | IEC 60216 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 Injection Molded |
4 168 h / 110°C |
【新闻资讯】查看全部
注塑行业现淘汰狂潮 企业管理亟需跟进
2021-04-04 搜料网资讯: 适者生存,不适者淘汰,进化论的原理同样适用于企业之间的生存法则。弱肉强食,每一个淘汰者的背后都有各种原因,但究其根本,原因大体一致,于企业而言,管理或 |
注塑行业现淘汰狂潮 企业管理亟需跟进 搜料网资讯:适者生存,不适者淘汰,进化论的原理同样适用于企业之间的生存法则。弱肉强食,每一个淘汰者的背后都有各种原因,但究其根本,原因大体一致,于企业而言,管理或许就是根本。 自去年上半年以来,珠三角、长三角及浙江等地区已有不少模具、注塑企业被淘汰。为什么会有大量模具企业、注塑企业出现倒闭现象呢?相关人士对这些淘汰的注塑企业进行了大量的实地调查,发现这些倒闭的注塑企业都有共同的特点,而且其倒闭的原因惊人的相似。 分析发现,在被淘汰的注塑企业中,其模具技术、管理水平都非常落后,一直都是凭经验做事,跟着问题后面跑;他们的经营思路二十几年都没变,管理混乱、生产效率低、料耗大、机位人手多、生产成本高。 其模具、注塑件的品质和交货期经常达不到客户的要求,模具、注塑生产订单逐步减少;对模具、注塑模具和注塑机的使用、维护、保养意识低,生产过程中模具故障/设备故障多、停产修机、修模频繁;把模具、注塑加工错误地当成劳动密集型行业去运作,依靠低廉的劳动力维持经营;这些模具、注塑企业对新技术、新材料、新设备、新工具的应用不够重视,没有与时俱进,导致企业的竞争力下降;不重视学习模具、注塑技术管理知识和人才培养,学习意识低,观念落后(不学习等于选择落后),缺乏核心竞争力。 倒闭的模具、注塑企业都是干了十几年、二十几年的“老”企业,自以为是,不思进取;对模具、注塑技术/管理人员的职业技能培训不重视,既不外训,也不内训,注塑技术管理水平一直处于十分落后状态,缺乏技术/管理创新能力;这些企业一味地追求“节约”,该花的钱舍不得花,该控制的没控制,不注重控制模具、注塑生产过程中的各种浪费现象,生产中浪费十分惊人,导致企业的利润日益微薄;不适应现代注塑企业环境的变化——面对塑胶原料价格的飞涨、招工困难、人工成本不断增加、产品加工价格下降、客户要求的不断提高、美元贬值、新劳动法的实施、出口退税政策的取消和行业的竞争越来越激烈的环境,以“不变应万变”,最终被市场残酷地淘汰掉。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。