牌号简介 About |
---|
合成橡胶SBR-1502是丁二烯与a-甲基苯乙烯在(4-8)°C温度下共聚而成,其中用作乳化剂的是歧化松香和合成脂肪酸皂或复合乳化剂的混合物。中等门尼粘度。产品特点:外观-浅黄色至棕色捆;重量为(30±1)kg;包装-塑料容器;保质期-自制造之日起一(1)年。 Synthetic rubber SBR-1502 is is obtained by copolymerization of butadiene with a-methylstyrene at a temperature of (4-8)°C where used as emulsifier is a mixture of disproportionated rosin and synthetic fatty acid soaps or complex emulsifiers. Medium Mooney viscosity. Product characteristics: Appearance - bale of light-yellow to brown color; weight of a bale - (30 ± 1) kg; packing - a plastic container; shelf life - one (1) year since the date of manufacture |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
45 到 57 | MU | ASTM D1646 |
结合苯乙烯 Combined with styrene |
21.0 到 24.0 | % | 内部方法 |
Organic Acid Organic Acid |
5.0 到 7.2 | % | ASTM D5774 |
Soap(Organic Acid) Soap(Organic Acid) |
< 0.25 | % | ASTM D5774 |
灰份含量 Ash Content |
< 0.60 | % | ASTM D5667 |
挥发物 Volatiles |
% | ASTM D5668 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D3185 | |
300% 应变 300% strain |
MPa | ASTM D3185 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D3185 |
备注 |
---|
2 CAS No. 68610-06-0 |
【新闻资讯】查看全部
大数据“杀熟”把隐性的价格歧视显性化
2022-04-25 近年来,大数据杀熟问题一直备受大众关注。一些企业利用包含了个人信息的大数据杀熟,对不同群体进行差别定价,实行价格歧视,让消费者十分反感。例如,在同样的时间和地点, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |