牌号简介 About |
---|
说明F920A是一种用于吹塑薄膜的高密度聚乙烯树脂。该等级设计用于在常规LLDPE吹膜设备中加工。特点:高透明度、高硬度、良好的加工性、与低密度聚乙烯和低密度聚乙烯的相容性、直立式包装袋、纸巾和毛巾外包装、标签、新鲜切割、与低密度聚乙烯和低密度聚乙烯混合包装。 Description F920A is a high-density polyethylene resins for blown film applications. This grade is designed to be processed in conventional LLDPE blown film equipment. Characteristics Excellent transparency and high stiffness Good processability Good compatibility with LDPE and LLDPE Applications Stand-up Pouches, Tissue & towel overwrap, Labels Fresh-cut produce packaging Blend with LDPE and LLDPE |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.956 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
49.0 | MPa | ASTM D882 |
TD,屈服,25 µm TD, yield, 25 µ m |
34.3 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm MD:25 µm |
g | ASTM D1922 | |
TD:25 µm TD:25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
去年江西装备制造业营收突破五千亿元
2022-02-14 2月11日,从江西省工业和信息厅获悉,2021年,江西装备制造业(不含汽车)实现营业收入5460亿元,三年年均增长17.1%;利润总额371亿元,三年年均增长20.5%,高于营业收入年均增速3.4个百 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |