Flexirene® CL 10是一种含抗氧化剂的丁烯共聚物线性低密度聚乙烯(C4-LLDPE),适用于高光学性能薄膜的浇铸挤出。主要用途Flexirene® CL 10推荐用于生产手动和自动包装机中使用的拉伸膜。在多层膜中,Flexirene® CL 10提高了全局配方的光学性能;此外,由于其高加工性,建议在必须达到高生产率时使用树脂。 Flexirene CL 10 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties. Main Application Flexirene CL 10 is recommended for the production of stretch film to be used both in manual and in automatic wrapping machines. In a multilayer film, Flexirene CL 10 enhances the optical properties of the global formulation; moreover, for its high processability, the resin is recommended whenever high productivity has to be reached. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.6 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,铸造薄膜 With oneself - dynamic, casting thin films |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
23 | µm | |
薄膜厚度 film thickness |
10 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,23 µm,铸造薄膜 1% secant, MD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
1% 正割,TD,23 µm,铸造薄膜 1% secant, TD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,23 µm,吹塑薄膜 MD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,23 µm,吹塑薄膜 TD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,23 µm,吹塑薄膜 MD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,23 µm,吹塑薄膜 TD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,23 µm,铸造薄膜 MD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
TD,断裂,23 µm,铸造薄膜 TD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
23 µm,铸造薄膜 23 µ m, cast thin film 2 |
g | ISO 7765-1 | |
撕裂强度 tear strength 3 |
ISO 6383-2 | ||
MD,23 µm MD,23 µm |
kN/m | ISO 6383-2 | |
TD,23 µm TD,23 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,23 µm,铸造薄膜 45 °, 23 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
23 µm,铸造薄膜 23 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Cast Film |
【新闻资讯】查看全部
武汉乙烯工程晋级改造 年产能将升至110万吨
2017-10-25 记者昨日从中韩石化武汉乙烯获悉,武汉乙烯将在现有年产80万吨乙烯的基础上,通过挖潜、改造,将乙烯生产能力扩至年产110万吨。 据悉,武汉乙烯脱瓶颈改造项目总投资42.7亿元,以武汉乙烯目前核心三机基础不动,主要塔壳体不动、内件改造为前提,在现有年产乙烯80万吨的基础上,改造4套装置、新建两套装置和公用工程系统改造等。 楚天都市报记者获悉,该项目计划于2018年9月开工,2020年建成投产。届时将通过进一步扩大产能,增产市场需要的高附加值化工产品,发挥现有装置 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |