Ultramid A 20 V25是一种基于聚酰胺66树脂的25%玻璃纤维增强红磷阻燃等级。本产品经过热稳定处理,以优化注塑成型。本产品为天然和黑色。 TECHNYL® A 20 V25 Natural is a Red Phosphorous flame retardant polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection moulding. This grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress. |
产品描述 Product Description
厂家:德国巴斯夫 BASF
类别:PA66 PA66
用途:电气/电子应用领域;工业应用;薄壁部件;绝缘材料;
颜色:黑色,自然色
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 热稳定性好; 阻燃; Flame Characteristics,Heat Stabilized,V-0
填料:玻璃纤维 25
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.38 | g/cm³ | ISO 1183/A |
吸水率 Water absorption Water absorption |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.1 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.75 | % | ISO 62 |
成型收缩率 Molding shrinkage Molding shrinkage |
|||
平行 parallel Parallel |
0.35 | % | |
垂直 normal Vertical normal |
1.2 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus Tensile modulus |
|||
23℃,干燥 dry 23 ℃, dry |
MPa | ISO 527-2/1A | |
23℃,湿润 cond. |
MPa | ISO 527-2/1A | |
拉伸强度 Tensile Stress Tensile Strength |
|||
断裂 break,23℃,干燥 dry Break, 23 ℃, dry dry |
MPa | ISO 527-2/1A | |
断裂 break,23℃,湿润 cond. Break, 23 ℃, wet cond |
MPa | ISO 527-2/1A | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂,23℃,干燥 dry Fracture, 23 ℃, dry dry |
% | ISO 527-2 | |
断裂,23℃,湿润 cond. Fracture, 23 ℃, wet cond |
% | ISO 527-2 | |
弯曲模量 Flexural modulus Flexural modulus |
|||
23℃,干燥 dry 23 ℃, dry |
MPa | ISO 178 | |
23℃,湿润 cond. 23 ℃, moist cond |
MPa | ISO 178 | |
弯曲强度 Flexural strength Flexural strength |
|||
23℃,干燥 dry 23 ℃, dry |
MPa | ISO 178 | |
23℃,湿润 cond. 23 ℃, moist cond |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched impact strength Charpy notched impact strength |
|||
-30℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eA | |
简支梁冲击强度 Charpy impact strength Charpy impact strength of simply supported beams |
ISO 179/1eU | ||
-30℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod notched impact strength Izod notched impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 180/1A | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 unannealed 1.8 MPa, unannealed |
℃ | ISO 75-2/-1 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-1/-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity Surface resistivity |
|||
干燥 dry Dry |
ohms | IEC 62631-3-2 | |
湿润 cond. Wet Cond |
ohms | IEC 62631-3-2 | |
体积电阻率 Volume resistivity Volume resistivity |
|||
干燥 dry Dry |
ohm·m | IEC 62631-3-1 | |
湿润 cond. Wet Cond |
ohm·m | IEC 62631-3-1 | |
介电强度 Electric strength Electric strength |
|||
0.8 mm 0.8 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity Relative permittivity |
|||
干燥 dry,100Hz Dry, 100Hz |
IEC 62631-2-1 | ||
湿润 cond.,100Hz Wet Cond, 100Hz |
IEC 62631-2-1 | ||
耗散因数 Dissipation factor |
|||
干燥 dry Dry |
E-4 | IEC 62631-2-1 | |
湿润 cond. Wet Cond |
E-4 | IEC 62631-2-1 | |
相比漏电起痕指数 Comparative tracking index Compared tracking index |
|||
解决方案 A Solution A |
IEC 60112 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
calss | UL 94 | |
1.60 mm 1.60 mm |
calss | UL 94 | |
3.20 mm 3.20 mm |
calss | UL 94 | |
灼热丝可燃性指数 Glow Wire Flammability Index Glow Wire Flammability Index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignition Temperature |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Oxygen index |
% | ISO 4589-2 | |
French Fire Index French Fire Index |
NF F16-101 | ||
French Smoke Index French Smoke Index |
NF F16-101 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
“十四五”自贸试验区会否再扩围?商务部回应了
2021-02-11 搜料网资讯: 十三五时期,我国自贸试验区几经扩围,发展到21个,形成覆盖东西南北中的改革开放创新格局。十四五期间,自贸试验区数量会否进一步增加? 在商务部3日召开的十三五 |
“十四五”自贸试验区会否再扩围?商务部回应了 搜料网资讯:“十三五”时期,我国自贸试验区几经扩围,发展到21个,形成覆盖东西南北中的改革开放创新格局。“十四五”期间,自贸试验区数量会否进一步增加? 在商务部3日召开的“十三五”时期自贸试验区建设情况发布会上,商务部自贸区港司司长唐文弘表示,商务部将根据中央决策部署,在充分评估现有21个自贸试验区建设成效基础上再统筹研究。 五年来,我国自贸试验区建设交出一份亮眼“成绩单”:被赋予更大改革自主权,总计被赋予2800多项改革试点任务;不断推动高水平对外开放,自贸试验区外商投资准入负面清单特别管理措施“十三五”初期为122项,2020年压减至30项,压减幅度超75%;探索形成173项制度创新成果向全国复制推广,共形成1300余项制度创新成果在地方推广。 根据商务部数据,2020年,前18家自贸试验区共新设企业39.3万家,实际使用外资1763.8亿元,实现进出口总额4.7万亿元,实现了占全国17.6%的外商投资和14.7%的进出口,为稳外贸稳外资发挥了重要作用。 “十四五”规划建议提出,完善自由贸易试验区布局,赋予其更大改革自主权,稳步推进海南自由贸易港建设,建设对外开放新高地。 商务部自贸区港司副司长袁园说,下一步,商务部将聚焦市场主体关切,推动更多深层次改革事项在自贸试验区先行先试;进一步加大对外开放力度,深入开展贸易投资自由化、便利化改革创新,制定出台自贸试验区跨境服务贸易负面清单;推动自贸试验区结合自身战略定位和特色产业开放进行制度创新。 袁园还表示,目前,商务部正在会同有关方面,抓紧推进海南自由贸易港跨境服务贸易负面清单相关工作。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。