牌号简介 About |
---|
AOC的Vipel F764系列是一种高交联间苯二甲酸聚酯树脂。AOC的Vipel F764系列树脂是为了满足含氧燃料的地下石油储罐的要求而开发的。UL认可AOC的Vipel F764系列树脂被UL认可,以满足UL 1316和UL 1746第二部分和第三部分的要求。耐腐蚀Vipel F764系列树脂在与无机和有机酸接触时提供优异的耐腐蚀性。许多燃料,包括汽油、煤油、加热油和原油,耐溶剂性已被现场证明。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀性信息或关于树脂是否适合任何特定化学环境的问题。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。 AOC's Vipel F764 Series is a high cross-linked isophthalic polyester resin. AOC's Vipel F764 Series resins were developed to meet the demanding requirements of underground petroleum storage tanks that contain oxygenated fuels. BENEFITS UL Recognition AOC's Vipel F764 Series resins are recognized by UL for meeting the requirements of UL 1316 and UL 1746 Part II and Part III. Corrosion Resistance Vipel F764 Series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many fuels including gasoline, kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion reistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
45 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
139 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
16.0 | min | |
放热峰值 exothermic peak |
218 | ℃ | |
触变指数 Thixotropic index 2 |
|||
25℃ 25℃ 2 |
2.00 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2/20 rpm |
【新闻资讯】查看全部
巴斯夫召回数千吨疑含致癌物产品
2017-10-13 多家泡沫制造商已经宣布临时停产,据新闻报道,这是由于位于德国路德维希港的巴斯夫工厂正在召回其制造的甲苯二异氰酸酯(TDI)所导致,欧洲市场也因而处于混乱的状态。 10月5日,德国化工领头企业巴斯夫公司告知客户由其位于路德维希港的工厂从8月25日至9月29日期间生产的TDI里二氯苯含量可能明显高于公司的标准含量。 因此,几家使用TDI作为原材料的泡沫制造商已经宣布临时停产,试图消化这则新闻报道带来的影响。 世界上最大的缓冲制品生产商Carpen |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |