Dowlex 2355聚乙烯树脂是一种乙烯-辛烯共聚物,由陶氏化学公司的专有溶液工艺生产。具有独特的分子结构,侧链分布可控,具有优异的抗应力开裂性能,并具有很好的长期静液强度。可加工性:Dowlex 2355聚乙烯树脂加工的典型挤压温度范围为190至230°C。使用反向温度曲线可能对某些类型的加工设备有利。有关更多信息,请参阅我们的挤出指南。应用:热水和冷水系统用管道,例如:地板加热墙加热/冷却天花板冷却散热器连接热水/冷水分配热回收系统太阳能电池板符合:欧盟,2011年第10号,美国食品和药物管理局21 CFR 175.105(c)(5)美国食品和药物管理局21 CFR 177.1520(c)3.2a(有限制)参考法规细节。 DOWLEX 2355 Polyethylene Resin is an ethylene-octene copolymer, produced in the proprietary solution process of The Dow Chemical Company. It has a unique molecular structure with a controlled side chain distribution, which provides excellent stress crack resistance properties combined with very good Long Term Hydrostatic Strength. Processability: Typical extrusion temperatures for processing of DOWLEX 2355 Polyethylene Resin range from 190 to 230° C. The use of a reverse temperature profile may be beneficial on certain types of processing equipment. For further information, see our Extrusion Guideline. Applications: Pipes for hot and cold water systems, e.g.: floor heating wall heating/cooling ceiling cooling radiator connections warm / cold drinking water distribution heat recovery systems solar panels Complies with: EU, No 10/2011 U.S. FDA 21 CFR 175.105(c)(5) U.S. FDA 21 CFR 177.1520(c)3.2a (with Restrictions) Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.931 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
2.3 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,10%乳化剂 50 ℃, 10% emulsifier |
> 8760 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
399 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
% | ISO 527-2 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:20~70℃ MD:20~70℃ |
1/℃ | DIN 53752 | |
导热系数 Thermal conductivity coefficient |
|||
60℃ 60℃ |
W/m/K | DIN 52612 | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
|||
邵氏 D,2.00 mm Shore D, 2.00 mm 2 |
ISO 868 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
【新闻资讯】查看全部
塑料味对海鸟有吸引力?海鸟吃塑料味道好极了
2016-11-15 到2050年,近200种海鸟――从企鹅到海燕――将以塑料为食。不过,是什么吸引它们吃下这些通常具有致死性的碎片?这不只是因为塑料和可口的水母或者海草“小食”看上去相似。一项最新研究显示,当被海藻附着时,塑料的气味也会对一些海鸟产生吸引力。 为探明这是如何发生的,研究人员将塞满3种塑料珠子的网眼编织袋绑在美国加州海岸的浮标上。他们发现,漂浮的珠子获得了一种被称为二甲基硫醚(DMS)的化学物质。DMS是海藻和其他微生物在分解时(即被吃掉时)释放出的一种副产物。由于吃掉海藻的是作 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |