牌号简介 About |
---|
Lupoy PC 1201-22树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。 LUPOY PC 1201-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
产品描述 Product Description
厂家:韩国LG化学 LG Chemical
类别:PC Polycarbonate
用途:包装;玩具;一次性餐具;电子电器产品;
加工条件:挤出,注射成型 Extrusion,Injection Molding
性能特点: 含脱模剂; 超高流动性; 耐高温; 防火阻燃等级V-2; 透光性好; 低粘度; 冲击性能好; 食品接触; Low Viscosity,High impact resistance,Good stripping performance,High Heat Resistance,Ultra high liquidity,Good Clarity,V-2,Food contact compliance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1200 | kg/m³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
22 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
0.005-0.007 | mm/mm | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃ 23℃ |
ASTM D256 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,3.20 mm,Total Energy 23℃,3.20 mm,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
0.45 MPa,退火,4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
50℃/hr,50N 50℃/hr,50N |
℃ | ASTM D1525 | |
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃,干燥 23 ℃, dry |
W-cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm 2.00 mm |
V | IEC 112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.50 mm 0.50 mm |
ASTM D635 | ||
1.60 mm 1.60 mm |
ASTM D635 | ||
2.50 mm 2.50 mm |
ASTM D635 | ||
3.00 mm 3.00 mm |
ASTM D635 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
平均燃烧程度 Average combustion degree |
mm | ASTM D635 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
耐磨耗性 Wear resistance |
|||
D雾度 D haze |
% | ASTM D1004 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
M Scale | ASTM D785 | |
R 级 R-level |
R Scale | ASTM D785 | |
落镖冲击,总能量23℃ Dart impact, total energy 23 ℃ |
J | ASTM D3763 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 1000g, 500 cycles, CS-10F Wheel |
4 9.8 mil 缺口深度 |
5 11.1 ft/sec |
6 速率 A (50°C/h), 载荷2 (50N) |
7 5 sec |
【新闻资讯】查看全部
浅析塑料制品防静电PVC板的施工标准
2017-10-26 塑料制品直铺导/防静电pvc板施工规范 一.材料、设备与工具 1.施工用材料应符合以下要求: (1) 、帖面板:物理性能及外观尺寸应符合《防静电贴面板通用规范》 SJ/T11236 的要求,并具有永久防静电性能。其体积及表面电阻:导静电型贴面板的电阻值应低于 1.0 ×106 Ω 。 (2) 、导电胶:应是非水溶性胶,电阻值应小于贴面板的电阻值,粘结强度应大于 3 × 106 N/m2 (3) 、塑料焊条:应采 |
浅析塑料制品防静电PVC板的施工标准 塑胶制品直铺导/防静电pvc板施工标准 一.原材料、机器设备与专用工具 1.施工用原材料应合乎下列规定: (1) 、帖控制面板:工艺性能及外型规格应合乎《防静电贴面板通用规范》 SJ/T11236 的规定,并具备永久性防静电特性。其容积及表面电阻率:导静电感应型贴面板的电阻值应小于 1.0 ×106 Ω 。 (2) 、导电胶:应是是非非水溶胶,电阻值应低于贴面板的电阻值,粘接抗压强度应超过 3 × 106 N/m2 (3) 、塑胶焊丝:应选用颜色匀称、直径一致、柔性好的原材料。 (4)、导电性避雷带用铜泊:薄厚应不小于 0.05mm ,宽宜为 20毫米 。 2.贴面板应存储在自然通风干躁的库房中,杜绝酸、碱以及他腐蚀化学物质。运送时要轻便轻卸,禁止死劲碰撞。禁止放置户外日晒淋雨。 3. 常见施工机器设备(含专用工具)应包含切槽机、塑料焊枪、硫化橡胶锤头、切刀、刻度尺 二、一般要求 1.防静电聚氯乙烯( pvc )路面施工內容包含农村基层解决、接地保护安裝、强力胶配备、防静电聚氯乙烯( PVC )贴面板(下称帖控制面板)的铺帖与清理等施工、检测及产品质量检验。 2.施工当场溫度应在 10― 35 ℃ 间;空气湿度不超 80% ;自然通风应优良而且确保 房间内别的各类工程项目施工应已基础完毕。 来源于:环球塑化网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 后车灯灯壳
- 2019-06-25 0
- Lupoy® 1300-03树脂是注塑成型的聚碳酸酯树脂。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。
- 阅读全文
后车灯灯壳
收起
抱歉!暂无数据。