牌号简介 About |
---|
Celanex® 3300是一种通用的30%玻璃增强聚对苯二甲酸丁二醇酯,它提供了机械、电气和热性能的优良组合。该牌号具有优异的加工性能和良好的耐化学性。Celanex® 3300是一种高流动性材料。 Celanex 3300 is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outstanding processability and good chemical resistance. Celanex 3300 is a high flow material. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PBT polybutylene terephthalate
用途:电气/电子应用领域;通用;
性能特点: 防火阻燃等级HB; 耐化学性; 流动性高; 易加工; Excellent Processability,High liquidity,Solvent resistance,HB
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.53 | g/cm³ | ASTM D792 |
密度 Density |
1.53 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,2.16 kg 250℃,2.16 kg |
17.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD MD |
0.30 to 0.50 | % | ASTM D955 |
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 3 |
kV/mm | ASTM D149 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
1 MHz 1 MHz |
ASTM D150 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.70 mm 0.70 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ASTM D638 | ||
-40℃ -40℃ |
MPa | ASTM D638 | |
0℃ 0℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ASTM D638 | |
80℃ 80℃ |
MPa | ASTM D638 | |
121℃ 121℃ |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
断裂,0℃ Fracture, 0 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture |
% | ISO 527-2/1A/5 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ASTM D638 | |
断裂,0℃ Fracture, 0 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ |
% | ASTM D638 | |
断裂,121℃ Fracture, 121 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
3 方法A(短时间) |
【新闻资讯】查看全部
REPSOL计划提高西班牙工厂聚合物多元醇的产量,并优化泡沫的性能
2022-06-01 西班牙能源集团Repsol表示,正在投资1800多万欧元,以提高其位于西班牙塔拉戈纳的工厂聚合物多元醇的产量。 西班牙能源集团Repsol 寻求通过第二个材料反应器来扩大产能,并通过用于 |
REPSOL计划提高西班牙工厂聚合物多元醇的产量,并优化泡沫的性能
西班牙能源集团Repsol表示,正在投资1800多万欧元,以提高其位于西班牙塔拉戈纳的工厂聚合物多元醇的产量。
西班牙能源集团Repsol寻求通过第二个材料反应器来扩大产能,并通过用于家具、床上用品和汽车的更高质量材料来增加产品组合。
西班牙能源集团Repsol表示,这项工作计划于2023年底完成,并将使用位于西班牙塔拉戈纳的工厂由Repsol技术实验室的科学家开发的新技术。“因此,工艺得到了优化,泡沫的性能以及硬度和拉伸性能得到了改善,满足了高端应用的要求。”
Repsol目前在塔拉戈纳经营一条Alcupol品牌多元醇生产线,总产能为140000吨/年。大部分产量为用于柔性泡沫应用的多元醇,而聚合物多元醇的生产量较小。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 冰箱紧缩机消声器
- 2019-01-25 0
- LG ABS HF380是一种丙烯腈丁二烯苯乙烯(ABS)材料。该产品在亚太地区、北美洲、拉丁美洲或欧洲有供货,加工方式为:注射成型。 LG ABS HF380的主要特性有: 阻燃/额定火焰 高流动性 典型应用领域包括: 生活消费品 电气/电子应用
- 阅读全文
冰箱紧缩机消声器
1-具有出色的机械强度,良好的硬度及刚性
2-要求热变形温度很高
3-要求良好的电气特性-绝缘性以及介电强度
4-要求良好的抗化性(氢氟碳化物、异丁烷、酯类油等)
5-要求良好的成型性
6-注塑成型
2-要求热变形温度很高
3-要求良好的电气特性-绝缘性以及介电强度
4-要求良好的抗化性(氢氟碳化物、异丁烷、酯类油等)
5-要求良好的成型性
6-注塑成型
收起
抱歉!暂无数据。