ICORENE® 1761是一种中等密度的茂金属聚乙烯,用于旋转成型。ICORENE® 1761适用于一般用途。它具有良好的韧性、易流动性、高冲击性和表面光泽等性能平衡。 ICORENE® 1761 is a metallocene linear low density polyethylene for rotational moulding applications. This grade is suitable for use in general purpose applications. It has a good balance of properties such as toughness, easy flow, high impact, and surface gloss. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.935 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
6.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693 | ||
10%非离子洗涤剂 10% non-ionic detergent |
> 300 | hr | ASTM D1693 |
100%非离子洗涤剂 100% non-ionic detergent |
> 1000 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服 yield |
18.0 | MPa | ISO 527-2 |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落下冲击阻力 Falling impact resistance 2 |
|||
-20℃ -20℃ 2 |
J/cm | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Based on ISO 6603 |
【新闻资讯】查看全部
新效果无望用于各种需要材料本身能自我修复的场景
2019-02-12 日本研究人员日前开发出一种切断后可自动修复的高分子材料,这一成果有望应用于各种需要材料本身能自我修复的场景。 日本理化学研究所和日本九州大学的研究团队使用一种稀土类金属钪作为催化剂,成功地在常压下将乙烯与苯甲酰丙烯合成了一种聚烯烃高分子材料,这种新材料具有极强的柔韧性和弹性,且像液体一样,即使将其切断也会依靠分子间的相互作用自动复原。 研究发现,这种材料不仅在空气中具备自我修复和形状记忆能力,在水中和酸中以及碱性水溶液中也同样具备这种能力,且不需额外施加任何 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |