牌号简介 About |
---|
Bayflex 110-35 IMR系统生产的固体聚氨酯弹性体在室温下的弯曲模量约为33500 psi*。该系统用于提供多种大型反应注射成型(RIM)零件,如汽车蒙皮。该系统包含内部模具释放(IMR),与磨制玻璃纤维或矿物增强材料一起使用。Bayflex 110-35 IMR是作为两种液体成分提供的配方RIM系统。A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇体系。与任何产品一样,在给定应用中使用Bayflex 110-35 IMR系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Bayflex 110-35 IMR system produces a solid urethane elastomer which has a flexural modulus of approximately 33,500 psi* at room temperature. This system is used to provide multiple releases of large reaction injection molding (RIM) parts, such as automotive fascias. The system contains internal mold release (IMR) and is used with milled glass fiber or mineral reinforcements. Bayflex 110-35 IMR is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. As with any product, use of the Bayflex 110-35 IMR system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR-脂肪族+MDI PUR-脂肪族+MDI
用途:饰带;汽车领域的应用;
加工条件:反应注射成型 (RIM)
填料:玻璃纤维/矿物
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 , ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.56 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
15.2 | MPa | ASTM D412 |
断裂,3.18 mm Fracture, 3.18 mm |
15.2 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
110 | % | ASTM D412 |
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ASTM D790 | |
23℃,3.18 mm 23℃,3.18 mm |
MPa | ASTM D790 | |
65℃,3.18 mm 65℃,3.18 mm |
MPa | ASTM D790 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 2 |
|||
3.18 mm 3.18 mm 2 |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(6 in Overhang,121℃,3.18 mm) Heat Sag(6 in Overhang,121℃,3.18 mm) 4 |
mm | ASTM D3769 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 3 |
|||
部件 A Component A |
|||
部件 B Component B |
|||
脱模时间 stripping time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 105 Index |
4 1 hr |
【新闻资讯】查看全部
古雷石化:EVA抢工期!乙烯装置“双烯”收率再创历史新高!
2022-05-13 又抢回56天!真是不容易啊! 古雷石化EVA装置压缩岗位副操李建军感慨道。4月29日,经过近一个月的不懈努力,装置循环水管线冲洗工作顺利完成,为装置投料试车提供了必要条件。 |
古雷石化:EVA抢工期!乙烯装置“双烯”收率再创历史新高!
“又抢回56天!真是不容易啊!” 古雷石化EVA装置压缩岗位副操李建军感慨道。4月29日,经过近一个月的不懈努力,装置循环水管线冲洗工作顺利完成,为装置投料试车提供了必要条件。
受中、高压设备安装进度影响,EVA装置内循环水管线施工滞后,循环水管线冲洗工作进度较慢,古雷石化化工二部为抢抓进度,主动出击、不等不靠,制定《循环水管线冲洗方案》和《消防水引入方案》,利用消防水对装置内所有循环水管线进行冲洗。由于冲洗工作量大,且施工单位配合人员较少,从准备工作开始,化工二部员工能自己解决的问题就自己解决,以昂扬向上、奋发有为的精神状态,认真做好拆卸管线、隔离设备、保护PLC系统面板等各项工作。通过努力,4月29日化工二部成功完成循环水冲洗工作,比原定计划提前了56天完成,为后续诸多工作顺利开展预留了充足时间。
“双烯”收率再破新高
今年以来,古雷石化面对严峻的市场形势,以搞好装置安全、稳定、长周期、优化生产为重点,深入挖潜增效、着力提高经济技术指标。5月1日,乙烯装置“双烯”收率达到51.7%,再创历史新高,其中乙烯收率34.9%、丙烯收率16.8% 。
自项目投产以来,古雷石化成立攻关小组,对提高“双烯”收率等主要经济指标开展技术攻关,摸索不同原料状况下最佳裂解深度,找出裂解炉的最佳运行工况。攻关小组经过坚持不懈地努力,基本摸索出不同原料组成下的最佳裂解深度。自2022年2月23日至今,“双烯”收率均在50.5%以上。这是古雷石化化工一部全体员工上百个日夜不断探索尝试后交出的满意答卷。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。