Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲。应用领域包括汽车、电气和家用领域的高压力设备外壳。 Ultradur S 4090 G6 is a 30% glass reinforced PBT+ASA blend. It produces moldings with good surface finish, is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors. |
产品描述 Product Description
厂家:德国巴斯夫 BASF
类别:PBT+ASA PBT+ASA
用途:电器外壳;汽车领域的应用;家用货品;外壳;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 耐化学性; 低翘曲性; 收缩性低; 抗应力开裂; 表面光泽度好; Solvent resistance,HB,Low contractility,Low warping,High ESCR,Good surface appearance
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.47 | g/cm³ | ASTM D792 |
密度 Density |
1.47 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,2.16 kg 275℃,2.16 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
MD:3.2 mm MD:3.2 mm |
0.30 | % | |
TD TD |
0.75 | % | ISO 294-4 |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
MPa | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
断裂,120℃ Fracture, 120 ℃ |
% | ISO 527-2 | |
断裂,150℃ Fracture, 150 ℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.69 mm 0.69 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.69 mm 0.69 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.69 mm 0.69 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.69 mm 0.69 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.5 mm |
【新闻资讯】查看全部
中国中化举行院校进企业交流活动
2021-08-15 搜料网资讯: 8月4日,中国中化举办第一期院校进企业科技创新交流活动,旨在进一步推进开放式创新,建立新型、高效的产学研合作交流长效机制和平台,帮助一线经营单位引入外部 |
中国中化举行院校进企业交流活动 搜料网资讯:8月4日,中国中化举办第一期“院校进企业科技创新交流活动”,旨在进一步推进开放式创新,建立新型、高效的产学研合作交流长效机制和平台,帮助一线经营单位引入外部优势科技资源。 此次活动围绕综合性化工业务在过程强化方面大量的技术需求,特邀中国工程院陈建峰院士课题组孙宝昌教授作专题报告。孙宝昌介绍了超重力反应强化的关键流程再造技术及工业应用情况,并和参会人员围绕硫化床气固反应、氨静置反应器脱硫、提高废水可生化性等研发、生产过程中遇到的实际困难和问题,进行沟通与交流。 超重力反应技术由陈建峰院士在国际上率先提出并实现工业化应用,对解决化工生产过程“三高”问题、提升效率和品质具有显著效果,已成功应用于高端化学品、纳米材料、脱硫环保、海洋工程、能源等流程工业中,相关技术装备在海内外已实现应用100余套。 中国中化各事业部、专业公司驻上海、江苏、四川、湖南、山东、浙江等地的130余位研发、工程、生产条线人员通过80个网络接口线上参加此次活动。中国中化将以此次交流活动为起点,推动相关项目研究论证和落地,继续有针对性地组织与外部高校、科研院所的研讨交流,借助外部科技资源促进公司工艺改进、产品升级,助力打造世界一流的综合性化工企业。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- Rover600侧后视镜壳体
- 2019-04-10 0
- Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物,它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲
- 阅读全文
Rover600侧后视镜壳体
1-Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物
2-熔体体积流动速率(275℃/2.16 kg),20.0 cm³/10min
2-熔体体积流动速率(275℃/2.16 kg),20.0 cm³/10min
3-悬臂梁缺口冲击强度(23℃),85 kJ/m²
4-热变形温度(0.45 MPa,未退火),210℃
收起
- 汽车电子控制安装衔接器
- 2019-01-25 0
- Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲
- 阅读全文
汽车电子控制安装衔接器
1-Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物
2-熔体体积流动速率(275℃,2.16 kg) 20.0 cm³/10min
3-收缩率(MD:3.2 mm) 0.30 %
4-弯曲模量(23℃) 8270 MPa
5-简支梁无缺口冲击强度(-30℃) 50 kJ/m²
6-热变形温度(1.8 MPa,未退火) 177 ℃
2-熔体体积流动速率(275℃,2.16 kg) 20.0 cm³/10min
3-收缩率(MD:3.2 mm) 0.30 %
4-弯曲模量(23℃) 8270 MPa
5-简支梁无缺口冲击强度(-30℃) 50 kJ/m²
6-热变形温度(1.8 MPa,未退火) 177 ℃
收起
- 汽车保险丝盒
- 2019-09-18 0
- Ultradur® S 4090 G6是一种30%玻璃增强PBT+ASA混合物。它生产的模具具有良好的表面光洁度,耐化学药品和应力开裂,具有低收缩和翘曲。应用领域包括汽车、电气和家用领域的高压力设备外壳。
- 阅读全文
汽车保险丝盒
1-具有良好的表面光洁度
2-具有出色的耐化学药品和应力开裂性能
3-具有低收缩和翘曲,尺寸稳定性好
4-具有出色的流动性能,易加工成型
5-具有高弯曲模量,机械性能好
6-受热变形温度高,耐高温性能好
2-具有出色的耐化学药品和应力开裂性能
3-具有低收缩和翘曲,尺寸稳定性好
4-具有出色的流动性能,易加工成型
5-具有高弯曲模量,机械性能好
6-受热变形温度高,耐高温性能好
收起