牌号简介 About |
---|
ASTALOY™ PC/ABS EHA是一种由ABS和聚碳酸酯制成的可电镀合金,设计用于注塑应用,需要平衡易选性、冲击韧性、产品刚度、耐热性和可塑性。汽车领域的典型应用包括电镀格栅、装饰和门把手。注:字母“U”或“W”表示已添加紫外线稳定[即:ASTALOY™ PC/ABS EHA7W]。 ASTALOY™ PC/ABS EHA is an electroplatable alloy of ABS and Polycarbonate and is designed for injection moulding applications requiring a balance of easy electoplatability, impact toughness, product rigidity, heat resistance and mouldability. Typical applications in the automotive field include electroplated grilles, garnishes and doorhandles. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS EHAW ]. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.09 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
250℃,3.80kg 250℃,3.80kg |
7.0 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
17 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
|||
3.2 mm 3.2 mm |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,12.7 mm 1.8 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.6 mm 1.6 mm |
℃ | AS/NZS 60695.2.12 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
3.20 mm 3.20 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,3.20 mm Fracture, 3.20 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
3.20 mm 3.20 mm 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
|||
3.20 mm 3.20 mm 3 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 0,051 in/min |
4 压 力1 (10N) |
【新闻资讯】查看全部
三聚氰胺树脂泡沫塑料运用前景
2017-07-25 三聚氰胺泡沫塑料由于优异的防火保温性已使有毒气体排放少,因此能够在很大程度上抑制恶性火灾的发生。随着技术的进一步发展、生产成本的下降,三聚氰胺泡沫塑料必将取代现今主流保温材料,迎来极大的市场发展机遇和挑战。 公安部2011年3月14日下发关于进一步明确民用建筑外保温材料消防监督管理有关要求的通知,在新标准发布前,从严执行《民用建筑外保温系统及外墙装饰防火暂行规定》(公通字[2009]46号)。规定中第二条为:民用建筑外保温材料采用燃烧性能为A级的材料。 近年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |