牌号简介 About |
---|
特点:均聚聚丙烯,清洁度高,加工性能稳定,规控性好,易拉伸,易取向,高速、低水携带。推荐用途:用于高速生产线中需要高强度和高强度的机织物的拉斐亚带、绳索、绳索、工业袋、地毯衬垫、大袋、通用挤压和注塑应用。 Characteristics: Homopolymer polypropylene with high cleanness and stable processability, excellent gage control, easy stretching and orientation to high speed and low water carry-over. Recommended for: Raffia Tapes for woven fabrics in high speed line where needs high tenacity and strength, ropes, cords, industrial bags, carpet backing, big bags, general purpose extrusion and injection molding applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate 1 |
|||
230℃,2.16kg 230℃,2.16kg 1 |
4.6 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 2 |
33.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
12 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
1380 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
43 | J/m | ASTM D256-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
3 类型 1, 2.0 in/min |
4 类型 1, 0.051 in/min |
【新闻资讯】查看全部
C8芳烃增产及转化技术开发与工业实验经过立项论证审查
2018-05-11 近日获悉,由辽阳石化公司牵头与石化研究院、昆仑工程公司、抚顺石化等单位联合申报的“C8芳烃增产及转化技术开发与工业试验”重大专项课题,已顺利通过中国石油集团公司科技管理部的立项论证审查。 芳烃与烯烃是炼化企业的两大支柱产品。近年来,国内市场对芳烃PX(对二甲苯)产品的需求量快速增长,每年我国需进口PX近60%。此项重大课题下设“已工业化的苯/重芳烃烷基转移技术的改进优化”“甲苯择形歧化技术的开发和放大”“两种C8芳烃异构化技术的改进开发”等3个专题,辽阳石化负责前两个课题的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |