牌号简介 About |
---|
Ultramid® T KR 4355 G5是一种25%玻璃纤维增强注塑成型PA6/6T级,具有高韧性、刚度和强度、低吸水性和高熔点(295 C)。材料经过处理后,其机械性能在65℃以下保持稳定。 Ultramid T KR 4355 G5 is a 25% glass fiber reinforced injection molding PA6/6T grade featuring high toughness, stiffness, and strength, low water absorption, and high melting point (295 C). After the material has been conditioned, its mechanical properties remain stable up to 65 C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 | g/cm³ | ISO 1183 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
5.5 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.3 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
9000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
214 | MPa | ISO 527-2 |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.44 mm 0.44 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
成核剂是一种新型功用塑料助剂
2017-08-30 成核剂是一种塑料助剂。成核剂适用于聚乙烯、聚丙烯等不完全结晶树脂,旨在通过改变树脂的结晶行为,加快结晶速度,增加结晶密度和促使晶粒尺寸微细化,达到缩短成型周期,提高制品透明性(此类成核剂亦称透明剂)、表面光泽、拉伸强度、刚性、热变形等物理机械性能的新型功能塑料助剂。 根据结晶形态可分为α-晶型成核剂和β-晶型成核剂。目前全球成核剂消费量约5kt/a,其中80%为二苯亚甲基山梨醇(DBS)类成核剂。由于能够改善PP的力学性能及 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |