牌号简介 About |
---|
Boltaron 9200是一种专利的挤压热塑性片材,设计用于飞机百叶窗。Boltaron 9200具有最大的遮光特性、优异的冲击强度、耐磨性、耐沾污性和耐化学性以及热成型性。Boltaron 9200符合FAA关于可燃性、烟雾产生和热释放的严格规定,如FAR 25.853第(a)和(d)段所述。Boltaron 9200提供单色(9200)或双色(9200C)结构。颜色:定制规格:0.047至0.060宽度:高达48英寸长度:高达120英寸纹理:粗糙哑光(cm)毛毡(ft)毛细胞(hc)莱凡特(lt)台面(ms)绒面革(sd) Boltaron 9200 is a proprietary, extruded thermoplastic sheet, designed for use as aircraft window shades. Boltaron 9200 offers maximum light blocking characteristics, excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Boltaron 9200 meets stringent FAA regulations for flammability, smoke generation and heat release as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9200 is available as a single color (9200) or as a double color (9200C) construction. Colors: Custom Gauges: .047 to .060 Widths: Up to 48" Lengths: Up to 120" Textures: Coarse Matte (CM) Felt (FT) Haircell (HC) Levant (LT) Mesa (MS) Suede (SD) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
53 到 110 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
75.6 到 77.8 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Ds Ds |
ASTM F814 | ||
1.5 min 1.5 min |
< 100 | ASTM F814 | |
4 min 4 min |
ASTM F814 | ||
成型温度 Forming temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
放热 exothermic |
FAR 25.853 | ||
2 min 2 min |
kW·min/m² | FAR 25.853 | |
Peak Peak |
kW/m² | FAR 25.853 | |
12 sec 12 sec |
|||
60 sec 60 sec |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
乙苯共氧化法高效绿色制备环氧丙烷成套技术
2019-01-09 1月5日,万华化学集团股份有限公司(以下简称万华化学)又一具有自主知识产权的高端技术打破国外公司技术垄断。“乙苯共氧化法高效绿色制备环氧丙烷成套技术”项目通过中国石油和化学工业联合会成果鉴定,由中国工程院陈建峰院士、蹇锡高院士以及中国科学院李亚栋院士等行业知名专家组成的专家委员会认为,该项目成果整体技术进入国际*行列。 环氧丙烷是*重点鼓励发展的高端石化产品,是支撑聚氨酯新材料、精细化工等产业发展非常重要的基础有机化工原料,其生产工艺主要有氯醇化法、共氧化法和直接氧化法。随 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |