牌号简介 About |
---|
PP H030 GP是一种具有标准分子质量分布的聚丙烯均聚物。该产品具有平均流动性、最佳的稳定包装和平衡的物理机械性能。 PP-H030-GP/1 is a polypropylene homopolymer with standard molecular weight distribution. The product is characterized by medium melt flow range, an optimal stabilization package and balanced physical and mechanical properties. TYPICAL APPLICATIONS PP-H030-GP/1 is a general purpose grade, it is recommended for Injection Moulding, Extrusion and Thermoforming applications. It complies with EU Food Contact Regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
34.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
10 | % | ISO 527-2/50 |
弯曲模量 Bending modulus 2 |
1400 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
2.0 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.20 in/min |
4 A (10N) |
【新闻资讯】查看全部
陶氏化学博得5亿美元专利侵权赔偿金
2017-07-14 Nova化学被加拿大联邦法院判定,向陶氏化学(DowChemical)支付5亿美元。这笔费用被认为是加拿大历史上专利侵权案中最大的一笔。 该案件可以追溯到2005年,涉及一系列使用Nova专利用于包括垃圾袋和食品包装在内的产品的聚乙烯树脂。Nova将聚合物以“SURPASS”的形式出售。 陶氏在2014年获得了对Nova的首次法庭审判,并于2016年得到上诉。有一次,Nova向Dow提出欺诈指控,但最终被撤销。 陶氏的回报是从Nova产品估计 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |